Reducing surface and bulk contamination in plastic

ABSTRACT

The present invention generally relates to a method of reducing contamination from plastics. The resulting purer plastic can be used in demanding applications.

FIELD OF THE INVENTION

The present invention generally relates to a method of producing a purer plastic from a first plastic. More specifically, the first plastic is subjected to bulk purification or surface and bulk purifications, wherein the total contamination present in the first plastic is reduced. The resulting purer plastic is sufficiently purer to allow for potential use in the demanding applications.

BACKGROUND OF THE INVENTION

Synthetic plastics are ubiquitous in daily life due to their relatively low production costs and good balance of material properties. They are used in a wide variety of applications, such as packaging, automotive components, medical devices, and consumer goods. To meet the high demand of these applications, hundreds of millions of tons of synthetic plastics are produced globally on an annual basis. The overwhelming majority of synthetic plastics are produced from increasingly scarce fossil sources, such as petroleum and natural gas. Additionally, the manufacturing of synthetic plastics from fossil sources causes the emission of greenhouse gases (GHG), primarily CO₂, in the atmosphere.

The ubiquitous use of synthetic plastics has consequently resulted in millions of tons of plastic waste being generated every year. While the majority of plastic waste is landfilled via municipal solid waste programs, a significant portion of plastic waste is found in the environment as litter, which is unsightly and potentially harmful to ecosystems. Also, plastic waste is leaked into the environment, e.g. washed into river systems and ultimately out to sea.

Plastics recycling has emerged as one solution to mitigate the issues associated with the poor management of the end-of-life of plastics. Recovering and re-using plastics diverts waste from landfills and reduces the demand for virgin plastics made from fossil sources, which consequently reduces GHG emissions. In developed regions of the world, such as the United States and the European Union, rates of plastics recycling are increasing due to greater awareness by consumers, businesses, and industrial manufacturing operations, and due to regulatory frameworks. The majority of recycled materials, including plastics (other than films), are mixed into a single stream which is collected and processed by a material recovery facility (MRF). At the MRF, materials are sorted, washed, and packaged (e.g. in bales) for resale. Plastics can be sorted into individual materials, such as single streams of high-density polyethylene (HDPE) and poly(ethylene terephthalate) (PET), or mixed streams of other common plastics (such as polypropylene (PP), low-density polyethylene (LDPE), poly(vinyl chloride) (PVC), polystyrene (PS), polycarbonate (PC), and polyamide (PA)). The single or mixed streams can then be further sorted, washed, and reprocessed at a plastics recovery facility (PRF) into pellets that are suitable for re-use in plastics processing, e.g., extrusion blow molding, profile extrusion, injection molding, and film making.

However, the utilization of these recycled plastics is currently limited due to contamination, which renders the plastics less valuable compared to virgin plastics. A key to increasing the recycle rates and lowering the CO₂ emissions and plastics pollution is to reduce the contamination to a level allowing broader utilization across more end markets, especially those involving demanding applications.

Films are a special case of recycled plastics and are predominately polyolefin in composition. Films offer unique challenges for recycling that have yet to be resolved. The recycled film supply stream can be split into two general categories: 1) pre-consumer recycle film, which includes both in-plant scrap/edge-trim that can be re-used in the same process that generated it and post-industrial recycle (PIR) film, which is film generated by internal plant waste that is not used in the same process that produced it; 2) post-consumer recycle (PCR) film including post-commercial recycle film, which is film that has been used in commerce but not directly by at-home consumers (e.g. back-of-store shrink wrap, pallet wrap, wholesale bags, furniture wrap, agricultural film, etc.) and post-household recycled film, which is film that has been used in commerce directly by at-home consumers (e.g. retail bags, retail food packaging, overwraps for diapers and hygiene products, trash bags, etc.). Post-industrial film waste for use in recycling is collected on a plant-by-plant basis for controlled end markets and may or may not involve (or require) significant cleaning steps before recycling. Post-commercial film is collected at the point of sale and transported to various PRFs specializing in film for various cleaning operations and eventual distribution to an end market. In the US, post-household film is primarily collected in store take-back programs where the end consumer returns the film to a collection bin at a local store. Film-based PRFs collect the film waste and deliver it to end markets after sortation and cleaning. The utilization of film recycled materials is quite limited due to contamination. The contamination of films is higher than other forms due to the high surface area to volume ratio which allows greater opportunity for external contamination. Currently, most film-based recycled plastics are down-cycled into markets that are not circular and are of limited size such as plastics lumber. As the collection of film-based waste grows, the need for end markets beyond plastics lumber is essential. Ideally, film-based waste will eventually discover a second life in film-based applications, thus ensuring ongoing circularity.

The end markets cannot grow unless contamination is greatly reduced. Considering the high volume of film that is used in the demanding applications, it is important that recycled plastics coming from these markets re-enter the same end markets to support circularity. As such, the ability to remove even greater levels of contaminants is critical to achieving circularity and reducing CO₂ emissions and plastics pollution. Plastics pollution is even more problematic for film considering the tremendous surface area per use and the mobility of the waste in the environment by both air and water.

While contamination is problematic for all end market applications, the demanding applications have even stricter requirements especially on certain chemical contaminants. The relevant chemical contaminants are grouped into various chemical classes depending on the chemical structure of the contaminants. Non-limiting examples of these chemical classes of contaminants are heavy metals, pesticides, dioxins, furans, polychlorinated biphenyls (PCBs), phthalates, polycyclic aromatic hydrocarbons (PAHs), organotins, bisphenols, isothiazolins, glyphosphate, alkyl phenols, alkylphenol ethoxylates, aromatic amines, and flame retardants. In addition, the target levels of these contaminants can be extremely low. For instance, the target levels may be on the order of parts per million (ppm), parts per billion (ppb), and parts per trillion (ppt), wherein the initial contaminated plastic may contain levels 1,000 times the targeted levels. Net, a 1,000× reduction in chemical contamination is often required.

Mechanical recycling, also known as secondary recycling, is a process of converting recycled plastic waste into a re-usable form for subsequent manufacturing. A more detailed review of mechanical recycling and other plastics recovery processes are described in S. M. Al-Salem, P. et al., Waste Management, 29(10) (2009), 2625-2643. Mechanical recycling of rigid plastics typically involves some form of surface washing followed by drying and melt densification. The melt densification step typically includes melt filtration and devolatilization. For film-based materials, there are dry and wet processes. In the dry process, a controlled film stream is typically shredded, dried, and then melt extruded into the final form. Melt filtration and devolatilization are typically part of the extrusion step. In wet processes, a controlled film stream is typically shredded, washed in an aqueous solution/solutions, dried, and then melt extruded into the final form. Melt filtration and devolatilization are typically part of the extrusion step. The above methods are generally acceptable at removing intentional surface contamination such as paper labels and unintentional surface contamination such as dirt but are poor at removing bulk contaminants.

U.S. Pat. No. 10,022,725 discloses a mechanical recycling method for cleaning linear low-density polyethylene (LLDPE)/LDPE film for use in recycling. The patent further discloses the steps of shredding, a first water washing step, a second size reduction step involving wet grinding, a friction washing step or steps where hot water is used in at least one step, a drying or multiple drying steps, and a compaction step. The method is likely to be quite effective at removing some surface contamination that is loosely bound but will be ineffective at removing bulk contamination due to extremely low solubility of the bulk contaminants in the aqueous washing media and/or limited diffusivity of the bulk contaminants within the plastic.

U.S. Pat. No. 9,616,595 discloses a mechanical recycling method for de-inking surface-printed plastic films. The patent further discloses steps of grinding, ink removal steps, general washing, recovery of the cleaning solution, recovering pigments, and drying. The ink removal step involves the use of an aqueous cleaning fluid with high pH and selective cleaning agents, such as dodecyl sulfate, and high turbulence. The method claims ability to remove surface printed ink, which potentially contributes to chemical contamination following heating in the recycling process. The process will have limited ability to remove bulk contaminants due to limited solubility of the bulk contaminants in the aqueous washing media and/or limited diffusivity of the bulk contaminants within the plastic.

To overcome the fundamental limitations of mechanical recycling, there have been many methods developed to purify contaminated plastics. Most of these methods use solvents to decontaminate and purify plastics. U.S. Pat. No. 7,935,736 discloses a method for recycling polyester from plastic waste using a solvent to dissolve the polyester prior to cleaning. This patent also discloses the need to use a precipitant to recover the polyester from the solvent.

U.S. Pat. No. 6,555,588 discloses a method to produce a polypropylene blend from a plastic mixture comprising other polymers. This patent discloses the extraction of contaminants from a polymer at a temperature below the dissolution temperature of the polymer in the selected solvent, such as hexane, for a specified residence time. The starting material is a porous pellet and the extraction conditions are below the melting temperature to enable conveyance in the process. This patent further discloses increasing the temperature of the solvent (or a second solvent) to dissolve the polymer prior to filtration. Further, the patent discloses the use of shear flow to precipitate polypropylene from solution. The polypropylene blend described in the patent contained up to 5.6 wt. % polyethylene contamination.

European Patent Application No. 849,312 discloses a process to obtain purer polyolefins from a polyolefin-containing plastic mixture or a polyolefin-containing waste. The patent application discloses the extraction of polyolefin mixtures or wastes with a hydrocarbon fraction of gasoline or diesel fuel with a boiling point above 90° C. at temperatures between 90° C. and the boiling point of the hydrocarbon solvent. The patent application further discloses contacting a hot polyolefin solution with bleaching clay and/or activated carbon to remove foreign components from the solution. Also, the patent application discloses cooling the solution to temperatures below 70° C. to crystallize the polyolefin and then removing adhering solvent by heating the polyolefin above its melting point, or evaporating the adhering solvent in a vacuum, or passing a gas stream through the polyolefin precipitate, and/or extraction of the solvent with an alcohol or ketone that boils below the melting point of the polyolefin.

U.S. Pat. No. 5,198,471 discloses a method for separating polymers from a physically commingled solid mixture (for example, waste plastics) containing a plurality of polymers using a solvent at a first lower temperature to form a first single-phase solution and a remaining solid component. The patent further discloses heating the solvent to higher temperatures to dissolve additional polymers that were not solubilized at the first lower temperature. Finally, the patent discloses filtration of insoluble polymer components.

U.S. Pat. No. 5,233,021 discloses a method of extracting pure polymeric components from a multi-component structure (for example, waste carpeting) by dissolving each component at an appropriate temperature and pressure in a supercritical fluid and then varying the temperature and/or pressure to extract particular components in sequence. However, similar to the U.S. Pat. No. 5,198,471, this patent only discloses filtration of undissolved components.

U.S. Pat. No. 5,739,270 discloses a method and apparatus for continuously separating a polymer component of a plastic from contaminants and other components of the plastic using a co-solvent and a working fluid. The co-solvent, at least partially, dissolves the polymer and the second fluid (that is in a liquid, critical, or supercritical state) solubilizes components from the polymer and precipitates some of the dissolved polymer from the co-solvent. The patent further discloses the step of filtering the thermoplastic co-solvent (with or without the working fluid) to remove particulate contaminants, such as glass particles.

U.S. Pat. No. 5,368,796 discloses a method for surface cleaning polyethylene films. The patent further discloses the steps of shredding, a first surface washing step (involving a boiling solvent at a temperature below the melting temperature of the polyethylene and at or near ambient pressure, while applying vigorous mechanical agitation for 30 min to rub the ink off), a second surface washing step (involving fresh solvent below the melting temperature of the polyethylene, while applying vigorous mechanical agitation for 30 min), a third surface washing step (involving the solvent below the melting temperature of the polyethylene, while applying vigorous mechanical agitation for 30 to 60 min, and devolatilization), and melt densification. Optionally, the method may include a water washing step prior to treatment with solvent to remove surface dirt. The patent further discloses that the solvent washing accomplishes extraction wherein the solvent does not dissolve the polymer. However, a small amount of wax, typically <1 wt. % may be removed. The solvent washing and extraction steps are further disclosed as occurring at the boiling point of the solvent, which is selected to be below the softening point of the polyethylene to avoid agglomeration. The above method is focused on the removal of surface printed inks and is silent on the removal of bulk permeable contaminants such as those described previously.

U.S. Patent Application No. 2009/0178693 discloses a method for purifying a plastic. The patent application further discloses a multi-step process involving granulation to form plastic chips, surface washing with supercritical CO₂, surface washing and extraction with a high boiling solvent or mixture of solvents (such as limonene and ethylene lactate), a final surface washing with supercritical CO₂ to remove the high boiling solvent on the surface, and devolatilization. Further disclosed is that the plastic chip feed material is stirred with the solvent and the shape of the chip is maintained. Also, it is disclosed that the recovered material remains as chips, which implies the process is completed at temperatures below the plastic's primary melting point.

U.S. Pat. No. 9,834,621 discloses a method for purifying polypropylene. The patent further discloses contacting the reclaimed polypropylene at a temperature from about 80° C. to about 280° C. and at a pressure from about 10 atm to about 544 atm with a first fluid solvent having a standard boiling point less than about 70° C., to produce an extracted reclaimed polypropylene; dissolving the extracted reclaimed polypropylene in a solvent selected from the group consisting of the first fluid solvent, a second fluid solvent, and mixtures thereof, at a temperature from about 90° C. to about 280° C. and a pressure from about 14 atm to about 544 atm to produce a first solution comprising polypropylene, at least one dissolved contaminant, and at least one suspended contaminant; settling the first solution comprising polypropylene, at least one dissolved contaminants, and at least one suspended contaminant at a temperature from about 90° C. to about 280° C. and at a pressure from about 14 atm to about 544 atm to produce a second solution comprising polypropylene, at least one dissolved contaminant, and less of the at least one suspended contaminant; filtering the second solution at a temperature from about 90° C. to about 280° C. and at a pressure from about 14 atm to about 544 atm to produce a third solution comprising purer polypropylene, at least one dissolved contaminant, and even less of the at least one suspended contaminant; and separating the purer polypropylene from the third solution; and where the second fluid solvent has the same chemical composition or a different chemical composition as the first fluid solvent. The above method is highly suitable for removing contamination. However, the ability to dissolve, settle, and filter plastics is quite difficult and may not be feasible or practical for plastics with high molecular weight (MW), such as those used in films and blow molded containers. In addition, the above method is silent on removing surface contamination prior to extraction and dissolution, thus increasing the burden on such disclosed processes, especially filtration.

In summary, the solvent-based methods to purify contaminated plastics, as described above, do not address the issue of removing both surface and bulk contaminants from plastics sufficiently and efficiently to enable utilization in demanding applications, particularly in films and rigid applications involving high MW plastics. Accordingly, there is a need for a method that: 1) produces a purer plastic, i.e., plastic without a significant amount of contamination; 2) is relatively simple in terms of the number of unit operations; and 3) can be used in high MW plastics, such as those sourced from film and rigid applications.

SUMMARY OF THE INVENTION

A method to extract contaminates from a first plastic to produce a purer plastic is provided that comprises providing a first plastic comprising individual contaminants, each individual contaminant having a concentration; extracting said individual contaminates from said first plastic at a temperature and a pressure, using a leaching solvent, in extraction stages, for a period of time and for a period of time per stage, to produce a purer plastic comprising individual contaminates, each having a concentration; wherein said extraction is flooded leaching wherein said temperature is below the primary melting point of the first plastic; wherein said extraction stages are conducted at a leaching solvent to first plastic mass ratio; wherein said leaching solvent to first plastic mass ratio per stage at any time is greater than about 5:1; wherein said pressure is between about atmospheric and 1,000 atm; wherein said first plastic individual contaminants comprise at least one of alkyl phenols, bisphenols, dioxins, PCBs, and phthalates; wherein each individual contaminate concentration in said purer plastic is reduced compared to each individual contaminate concentration in said first plastic; and wherein the average of said reductions of said concentrations of said first plastic contaminants to said purer plastic contaminants is at least about 55% or LOQ.

DETAILED DESCRIPTION OF THE INVENTION I. DEFINITIONS

As used herein, the term “plastic” refers to polymer, such as polyethylene (PE), PP, PET, LLDPE, LDPE, HDPE, polyethylene co-polymers, ethyl vinyl acetate copolymer (EVA), ethyl vinyl alcohol copolymer (EVOH), ethylene acrylic acid copolymer (EAA), PS, PC, PVC, PET, SBS, PA, etc., or mixtures thereof. Such polymers are characterized by high molecular weight, which generally determines melt processability and solid-state mechanical properties. For the purposes of the present invention, the terms “polymer” and “plastic” are used interchangeably, and the term “MW” refers to the weight-average molecular weight of the polymer.

As used herein, the term “reclaimed plastic” refers to re-grind, post-industrial, post-commercial, or post-household plastic of various forms including film, fiber, non-woven, and rigid packaging.

As used herein, the term “recycled plastic” refers to reclaimed plastic converted to a form that is used in making products and packaging either in blends with virgin plastic or by itself. The recycled plastic may be purer than the reclaimed plastic or may be identical except in form.

As used herein, the term “Pre-Consumer Plastic” refers to plastic waste that has not met its intended end purpose and has not been used in commerce or used by end consumers. Pre-Consumer Plastic has two subcategories of reclaim including 1) Internal Scrap/regrind and 2) Post-Industrial. Internal scrap/regrind is different from Post-Industrial in that Post-Industrial is not re-usable in the same process in which it was produced. Recycle resulting from Post-Industrial reclaim is referred to as Post-Industrial Recycle or PIR.

As used herein, the term “Post-Consumer Plastic” refers to plastic reclaim that has met its intended end purpose and has been used in commerce. Post-Consumer Plastic has two subcategories of reclaim including 1) Post-Commercial Plastic and 2). Post-Household Plastic. Post-commercial plastics includes plastics that have been used in commerce and have met their desired purpose. Examples include back of store reclaim and wholesale bags. Post-household plastics include plastics that have been used in homes of retail consumers. Examples include front of store plastics, retail bags, retail packaging, etc. Recycle resulting from Post-Consumer Plastic reclaim is referred to as Post-Consumer Recycle or PCR.

As used herein, the term “first plastic” refers to the plastic which is fed into the purification process and has a level of contamination that may include both surface and bulk contamination. Non-limiting examples of first plastic are reclaimed film and reclaimed HDPE bottles.

As used herein, the term “purer plastic” refers to the plastic which is produced by the purification process from a first plastic. The purer plastic has a level of contamination that is generally lower than that of the first plastic.

As used herein, the term “1^(st) Life plastic” refers to a virgin plastic that has not been utilized in its polymer form for any purpose.

As used herein, the term “contaminant” refers to any undesirable material contained on or within the plastic. The term “chemical contaminant” refers to any undesirable chemical species on the surface of the plastic or within the bulk of the plastic and comprises the molecular or elemental composition of the contaminant. The terms may be used interchangeably depending upon the intent. For example, paper contamination comprises cellulose. Net, cellulose would be one chemical contaminant within the paper contaminant. As used herein, the term “contamination” refers to the sum of all contaminants and the term “chemical contamination” refers to the sum of all chemical contaminants. The chemical contaminants are grouped in classes, which include chemical contaminants that have similar chemical structure. For example, As, Hg, and Cr are chemical contaminants in the “heavy metals” classification. Each contaminant may have different chemical attributes, such as solubility and diffusivity in the plastic, and target levels depending upon concentration and end use market.

As used herein, the term “surface contaminant” refers to a contaminant that is on the surface of the plastic. Similarly, the term “surface chemical contaminant” refers to the molecular or elemental composition of the surface contaminant. The surface contaminant may be attached to the surface of the plastic either loosely through physical attraction forces, or more strongly through polar or other forces. In general, a surface contaminant will have less than about 80% of its surface area embedded in the plastic.

As used herein, the term “bulk contaminant” refers to a contaminant that is in the bulk of the plastic. Similarly, the term “bulk chemical contaminant” refers to the molecular or elemental composition of the bulk contaminant. In general, a bulk contaminant will have more than about 80% of its surface area embedded in the plastic.

As used herein, the term “surface contamination” and “surface chemical contamination” refers to the sum of all surface contaminants and all surface chemical contaminants, respectively.

As used herein, the term “bulk contamination” and “bulk chemical contamination” refers to the sum of all bulk contaminants and all bulk chemical contaminants, respectively.

As used herein, the term “total contamination” refers to the sum of the surface contamination and bulk contamination and the sum of all the surface chemical contamination and bulk chemical contamination, respectively.

As used herein, the term “permeable contaminant” refers to a chemical contaminant that is both soluble and diffusible in the plastic. Non-limiting examples of permeable contaminants are formaldehyde, bisphenol A, and naphthalene.

As used herein, the term “impermeable contaminant” refers to a chemical contaminant that is either insoluble or non-diffusible in the plastic. Non-limiting examples of impermeable contaminants are heavy metals and gel particles composed of cross-linked or ultra-high molecular weight plastic (too large to diffuse).

As used herein, the term “permeable contamination” is the sum of all permeable contaminants and the term “impermeable contamination” is the sum of all impermeable contaminants. The sum of all permeable and impermeable contamination is the “chemical contamination” if described in molecular or elemental terms or just simply “the contamination” if described in general terms (such as cellulose vs paper).

As used herein, the term “intentional contaminant” refers to a contaminant that is intentionally added by the supply chain for a specific purpose to benefit the producer, retailer, or consumer, but may not be desired in the recycled plastic. Examples include print, paper labels, adhesives for labels, pigments (such as TiO₂), process additives (such as antioxidant (AO)), etc., that are necessary for marketing, branding, processability, and/or end use performance. As used herein, the term “intentional chemical contaminant” refers to an intentional contaminant described by its chemical composition. As used herein, the term “intentional contamination” refers to the sum of all intentional contaminants and the term “intentional chemical contamination” refers to the intentional contamination described by its chemical composition.

As used herein, the surface area to volume ratio of the a plastic is calculated as follows: For generally spherical objects like pellets, ground pellets, micronized pellets, etc., the surface area to volume ratio is calculated by 3/r; where r is the mass average radius. For generally flat and thin objects like film, the surface area to volume ratio is calculated by 2/t; where t is the mass average thickness. For generally long columnar objects like fibers, the surface area to volume ratio is calculated by 2/r; where r is the mass average radius.

As used herein, the term “unintentional contaminant” refers to any contaminant not intentionally added. Examples include dirt and cross-contamination that is not intentionally added by the producer, retailer, or consumer. As used herein, the term “unintentional chemical contaminant” refers to an unintentional contaminant described by its chemical composition. As used herein, the term “unintentional contamination” refers to the sum of all unintentional contaminants and the term “unintentional chemical contamination” refers to the unintentional contamination described by its chemical composition.

As used herein, the term “densified” refers to a state of plastic in which the bulk density of the plastic is higher than the bulk density of the original/pre-densified plastic and the original surface of the plastic is reduced and/or rendered inaccessible to wetting fluids. The process of producing a densified material is referred to as densification.

As used herein, the term “melt densification” refers to densification done near, at, or above the primary melting point of the plastic. Non-limiting methods of melt densification include melt extrusion and agglomeration with equipment, such as the Herbold HV series plastcompactor.

As used herein, the term “primary melting point” refers to the peak melting point (highest endothermic peak on a zero-slope baseline) of the plastic as measured using Differential Scanning calorimetry (DSC). For the purposes of the present invention, the terms “primary melting point”, “melting point”, “melting temperature”, and “primary melting temperature” are used interchangeably. For amorphous materials and/or materials lacking a distinct melting point, the defining temperature will be the approximate softening point of the material, which may be best characterized by the glass transition temperature. Those skilled in the art will understand the appropriateness of the criteria for non-semi-crystalline materials.

As used herein, the term “hexanes” refers to a blend of hexane isomers, such as normal hexane (at least 45 vol %, and typically, about 53 vol %), iso hexane (2-methylpentane, 3-methylpentane, and 2,3-dimethylbutane), and neo hexane (2,2-dimethylbutane).

As used herein, the term “limit of quantification” or “LOQ” refers to the lower detection limit for a given chemical contaminant as determined by the analytical methods disclosed in section IX. The LOQ is a function of the methods used and may vary from test method to test method. The LOQ used herein is specific to the method listed in section IX.

As used herein, the term “ppm” refers to parts per million, “ppb” refers to parts per billion, and “pptr” refers to parts per trillion.

II. FIRST PLASTIC

Plastics are predominately free of contamination (virgin plastics) when first produced at resin suppliers, such as Dow, Nova, ExxonMobil, etc. However, during the plastic's lifecycle (from production through distribution, consumer utilization, and eventual recycling) contamination is introduced either intentionally or unintentionally.

Non-limiting examples of intentional contamination include surface print, paper labels, adhesives for labels, pigments (such as TiO₂), process additives (such as antioxidant (AO)), etc., that are necessary for marketing, branding, processability, and/or end use performance. Non-limiting examples of unintentional contamination are dirt, cross-contamination, certain heavy metals, pesticides, dioxins, furans, PCBs, etc. Also, unintentional contamination can be produced from reactions involving intentional contaminants, such as the oxidation of paper labels to dioxins, degradation of adhesives or print binders, etc. Most of the latter occurs during melt densification methods used during the recycling process. Further, oxidation of the plastic during melt processing steps, such as those used for original package or product creation and/or latter recycling, will produce unintentional contamination, such as gels. In addition, unintentional contamination may result from interaction with products. For example, packaging materials that contain cleaning mixtures (e.g. limonene, surfactants, etc.), food (e.g. various organics), etc., will potentially become contaminated with such products. Finally, unintentional contamination can enter the plastic during production, e.g. contamination of a plastic with reaction by-products, unreacted monomers, etc.

It is recognized that different reclaimed plastic sources have different contamination and associated risks. Clearly, reclaimed plastic streams of unknown origin and lifecycle will be most abundant but also represent the highest potential for contamination. On the other side, controlled reclaimed plastic streams are available and represent lower potential risk for demanding applications. For instance, if a reclaimed plastic stream is known to be from demanding applications, then such reclaimed plastic stream will not contain any undesirable contaminants up to the point of distribution to the consumer else these plastics would not have been approved for use in these applications. As such, contamination preventing re-use in these same applications would primarily be unintentional contamination, which must originate from external sources and enter the plastic through surface contamination. A small amount of contamination could result from reactions involving intentional contamination such as oxidation of cellulosics to dioxins during melt densification.

Pre-consumer plastic generally has the lowest level of contamination due to its known composition and controlled history. It may include intentional contamination, such as surface print and opacifiers, but because these are known and controlled, it is quite easy to find applications tolerating such known contaminants. In addition, pre-consumer plastic tends to have low amounts of unintentional contamination due to the controlled history preventing external contamination. Thus, pre-consumer plastics that were originally destined for use in demanding applications will be ideal sources of reclaimed plastic for the same end markets with minimal cleaning/purification. The latter pre-consumer plastic in the form of film is referred to as “Approved Sourced Post-Industrial Film” (ASPIF). On the downside, the ASPIF stream is very limited in supply and does not support circularity.

Post-consumer plastics are generally more contaminated than pre-consumer plastics. The post-commercial subclass of post-consumer plastic has the next lowest level of contamination relative to pre-consumer recycle considering the somewhat controlled life cycle within the commerce supply chain. In general, post-commercial reclaim plastic will have a known and controlled level of intentional contamination, thus enabling broad utilization as reclaimed plastic. However, unintentional contamination is known to be ubiquitous and problematic with this stream, which prevents broad usage in demanding applications. Post-commercial plastic that is sourced from demanding applications, will be potentially usable back into these fields following adequate cleaning/purification. Post-commercial plastic sourced from demanding applications in the form of film is referred to as “Approved Source Post-Commercial Film” (ASPCF). To accommodate the on-going need of purer reclaimed plastic, recycle material suppliers have recently introduced post-commercial film sources with more controlled and known history. These new sources are called High-Custody sources and are primarily utilized with the post-commercial film stream. Net, High-Custody Post-Commercial film sources should have reduced level of contamination relative to general Post-Commercial film sources. On the downside, these High-Custody sources are of limited volume and are more costly.

The post-household subclass of post-consumer has the highest level of contamination considering the uncontrolled life cycle within the commerce channel. Such plastic has high levels of both intentional and unintentional contamination that is highly variable, unknown, and uncontrolled. Such plastic may include plastic sources that were originally unacceptable for use in demanding applications. As such, there are limited markets for this plastic source and essentially none in the demanding applications.

Surprisingly, plastics made purer by the present invention may allow source plastics from post-industrial (both ASPIF and uncontrolled source), post-commercial (both ASPCF and uncontrolled source), and post-household plastic to be used more broadly in the demanding applications with some limitations. In addition, most recycle material customers desire purer materials beyond what is available today and the purer plastics of the present invention meet this broader need for purer plastics from any source.

For the purposes of the present invention, non-limiting examples of plastic are film, sheet, injection molded parts, blow molded parts, fiber, nonwovens, wovens, thermoformed parts, and extruded strands.

The first plastic can be a virgin plastic or a reclaimed plastic. Also, the first plastic can be a first-life plastic (has been used only once before it entered the reclaimed plastic stream), second-life plastic (has been used twice before it entered the reclaimed plastic stream), or higher-life plastic (has been used many times before it entered the reclaimed plastic stream). In embodiments of the present invention, the first plastic comprises a reclaimed plastic. In another embodiment of the present invention, the first plastic comprises a virgin plastic. In one embodiment of the present invention, the first plastic comprises film. In yet another embodiment of the present invention, the first plastic is selected from the group comprising film, injection molded part, blow molded part, fiber, nonwoven, woven, thermoformed part, extruded strand, or mixtures thereof.

In embodiments of the present invention, the first plastic comprises a regrind/edge-trim/in-plant waste plastic. In another embodiment of the present invention, the first plastic comprises a post-industrial plastic. In yet another embodiment of the present invention, the first plastic comprises a post-industrial film. In yet another embodiment of the present invention, the first plastic comprises a post-industrial non-woven. In yet another embodiment of the present invention, the post-industrial film is ASPIF. In embodiments of the present invention, the first plastic comprises a post-commercial plastic. In another embodiment of the present invention, the first plastic comprises a post-commercial film. In another embodiment of the present invention, the first plastic comprises a post-commercial non-woven. In yet another embodiment of the present invention, the post-commercial film is ASPCF. In yet another embodiment of the present invention, the first plastic comprises High-Custody post-commercial film. In embodiments of the present invention, the first plastic comprises a post-household plastic. In another embodiment of the present invention, the first plastic comprises a post-household film. In yet another embodiment of the present invention, the first plastic comprises a post-household non-woven.

In embodiments of the present invention, the first plastic comprises polystyrene, co-polystyrene, polyamides, co-polyamides, polycarbonates, thermoplastic elastomers, styrenic block copolymers, polyesters, co-polyesters, polyvinylalcohols, pvcs, and copolymers of any of the above and mixtures of any of the above. In embodiments of the present invention, the first plastic comprises polyolefins, polyolefin copolymers, and polyolefin polar copolymers. In another embodiment of the present invention, the first plastics comprises LDPE and LLDPE copolymers. In another embodiment of the present invention, the first plastic comprises PP. In yet another embodiment of the present invention, the first plastic comprises HDPE and HDPE copolymers. In embodiments of the present invention, the first plastic comprises film, and the film comprises polyethylene and polyethylene copolymers.

The first plastic may be in many forms including but not limited to pellets, micronized pellets, ground pellets, shredded film, shredded or ground injection molded parts, shredded or ground blow molded parts, thermoformed parts, shredded nonwoven or woven, extruded strands, or agglomerated particles. In embodiments of the present invention, the first plastic comprises pellets.

III. CONTAMINANTS AND CONTAMINATION

Contaminants can generally be broken down into two migration categories: 1) permeable; and 2) impermeable. Contaminants that are permeable have solubility and diffusivity in the first plastic to allow migration into, through the plastic, and out of the plastic due to a chemical potential gradient. In other words, permeable contaminants and the grouping called permeable contamination are mobile. Impermeable implies that the contaminant does not have sufficient solubility and diffusivity to significantly move into, through the plastic, and out of the plastic. In other words, impermeable contamination represented by the summation of all impermeable contaminants is essentially immobile. Net, wherever impermeable contamination is first deposited, such contamination will remain in that location until physically removed, convectively transferred, or placed in contact with a different material which is permeable to the contaminant.

The chemical contaminants in the first plastic may be numerous but generally fall into one of several relevant chemical classes. Representative classes comprise pesticides, aldehydes, allergic fragrances, izioalines, alkylphenol ethoxylates, alkylphenols, bisphenols, dioxins, dioxin-like, furans, PCBs, organotins, metals, phthalates, polyaromatic hydrocarbons (PAHs), etc. Only some of these chemical classes are routinely found in pre- and post-consumer reclaim materials including pesticides, alkylphenol ethoxylates, alkylphenols, bisphenols, dioxins, dioxin-like, furans, PCBs, metals, organotins, phthalates, and PAHs.

Using the analytical methods disclosed in section IX Methods, the LOQs of the various contaminants may differ by orders of magnitude. For example, the LOQ of a typical pesticide is about 10 ppb; the LOQ of typical alkylphenol ethoxylate is about 50 ppb; the LOQ of a typical alkylphenol is about 5 ppb; the LOQ of bisphenol-A is about 5 ppb; the LOQ of typical dioxin is about 0.2 pptr; the LOQ of a typical furan is about 0.2 pptr; the LOQ of a typical PCB is about 5 pptr; the LOQ of a typical heavy metal is about 100 ppb; the LOQ of a typical organotin is about 300 pptr; the LOQ of typical phthalate is 50 ppb; the LOQ of a typical PAH is 1 ppb.

Several films sources were broadly classified for chemical contamination including three ASPIF sources, three High-Custody Post-Commercial Film sources, three Post-Commercial film sources, and one Post-Household film source using the analytical methods disclosed in section IX Methods, as shown in TABLES 1a-1i. Note: To simplify the presentation of chemical contamination results, the concentration data is displayed in terms of LOQ instead of absolute weight fraction. For example, if the contaminant concentration is 10 ppm and the LOQ is 1 ppm, then the concentration would be 10× LOQ or just 10 displayed in the data tables.

TABLES 1a-1i Chemical Contamination of ASPIF, High-Custody Post-Commercial (HCPC), Post-Commercial (PC), and Post-Household (PH) Film Sources

TABLE 1a Pesticide Chemical Contamination ASPIF HCPC PC PH Parameter #1 #2 #3 #1 #2 #3 #1 #2 #3 #1 Pesticides xLOQ xLOQ xLOQ xLOQ Pendimethalin <1 <1 <1 <1 <1 <1 <1 <1 <1 1.4 Diethyltoluamide (DEET) <1 <1 <1 <1 <1 <1 <1 <1 <1 3.7 Piperonyl butoxide <1 <1 <1 <1 <1 <1 1.0 12.0 28.0 6.6 Phenylphenol, ortho- <1 <1 <1 <1 <1 <1 1.1 <1 <1 <1 Chlorprofam <1 <1 <1 <1 <1 <1 <1 <1 <1 1.3 Permethrin <1 <1 <1 <1 <1 <1 <1 <1 <1 3.0

TABLE 1b Alkyl Phenol Ethoxylates Chemical Contamination ASPIF HCPC PC PH Parameter #1 #2 #3 #1 #2 #3 #1 #2 #3 #1 Alkylphenol ethoxylates xLOQ xLOQ xLOQ xLOQ 4-t-Octylphenolmonoethoxylate <1 <1 <1 <1 <1 <1 10.6 <1 4.2 9.4 4-t-Octylphenoldiethoxylate <1 <1 <1 <1 <1 <1 5.2 <1 3.6 9.0 4-t-Octylphenoltriethoxylate <1 <1 <1 <1 <1 <1 4.2 <1 5.0 6.6 4-t-Octylphenoltetraethoxylate <1 <1 <1 <1 <1 <1 4.4 <1 5.6 8.4 4-t-Octylphenolpentaethoxylate <1 <1 <1 <1 <1 <1 2.6 <1 6.0 11.2 4-t-Octylphenolhexaethoxylate <1 <1 <1 <1 <1 <1 5 <1 6.2 17.4 iso-Nonylphenolmonoethoxylate <1 <1 <1 <1 <1 <1 2.4 1.7 <1 4.0 iso-Nonylphenoldiethoxylate <1 <1 <1 <1 <1 <1 2.8 8.6 <1 28.0 iso-Nonylphenoltriethoxylate <1 <1 <1 <1 <1 <1 3.2 6.2 5.8 32.0 iso-Nonylphenoltetraethoxylate <1 <1 <1 <1 <1 <1 1.8 4.2 6.2 22.0 iso-Nonylphenolpentaethoxylate <1 <1 <1 <1 <1 <1 2.2 <1 6.2 19.2 iso-Nonylphenolhexaethoxylate <1 <1 <1 <1 <1 <1 <1 <1 <1 12.0

TABLE 1c Alkyl Phenols Chemical Contamination ASPIF HCPC PC PH Parameter #1 #2 #3 #1 #2 #3 #1 #2 #3 #1 Alkylphenols xLOQ xLOQ xLOQ xLOQ iso-Nonylphenol 2.2 <1 320.0 190.0 120.0 86.0 920.0 168.0 260.0 300.0 4-tert-Butylphenol <1 <1 <1 3.8 1.2 <1 2 2.4 <1 6.8 4-tert-Pentylphenol <1 24.0 550.0 19.4 52.0 40.0 1660.0 3.6 116.0 1720.0

TABLE 1d Bisphenols Chemical Contamination ASPIF HCPC PC PH Parameter #1 #2 #3 #1 #2 #3 #1 #2 #3 #1 Bisphenols xLOQ xLOQ xLOQ xLOQ Bisphenol A <1 <1 <1 46,000.0 1800.0 114.0 4.8 320.0 760.0 144

TABLE 1e Dioxins, Furans, and PCBs Chemical Contamination Parameter ASPIF HCPC PC PH Dioxins and #1 #2 #3 #1 #2 #3 #1 #2 #3 #1 dioxinlike and PCB xLOQ xLOQ xLOQ xLOQ 1,2,3,4,7,8-HxCDD <1 <1 <1 <1 <1 <1 <1 <1 <1 1.9 1,2,3,6,7,8-HxCDD <1 <1 <1 <1 <1 <1 <1 <1 6.1 7.4 1,2,3,7,8,9-HxCDD <1 <1 <1 <1 <1 <1 <1 <1 3.8 4.5 1,2,3,4,6,7,8-HpCDD <1 <1 <1 2.8 <1 3.4 3.8 10.9 84.5 63.0 OCDD <1 <1 <1 11.1 2.6 8.9 39.6 17.2 205.0 308.5 2,3,7,8-TCDF <1 <1 <1 2.6 1.8 1.2 2.6 4.7 <1 16.5 1,2,3,7,8-PeCDF <1 <1 <1 <1 <1 <1 <1 <1 2.7 <1 2,3,4,7,8-PeCDF <1 <1 <1 <1 <1 <1 <1 <1 <1 2.1 1,2,3,4,7,8-HxCDF <1 <1 <1 <1 <1 <1 <1 <1 3.3 2.0 1,2,3,6,7,8-HxCDF <1 <1 <1 <1 <1 <1 <1 <1 2.2 1.3 1,2,3,4,6,7,8-HpCDF <1 <1 <1 <1 <1 <1 1.29 <1 7.9 6.2 OCDF <1 <1 <1 <1 <1 <1 5.45 <1 6.5 13.8 PCB 77 <1 <1 <1 26.8 13.4 12.2 8.25 2.7 39.2 83.0 PCB 81 <1 <1 <1 46.4 19.9 21.8 10.58 5.6 88.2 79.4 PCB 126 <1 <1 <1 11 6.3 13.3 19.1 2.9 65.2 128.8 PCB 169 <1 <1 <1 <1 <1 <1 <1 <1 <1 11.2 PCB 105 <1 <1 <1 24.6 9.9 9.2 35.2 19.8 157.2 116.4 PCB 114 <1 <1 <1 1.9 <1 <1 2.22 1.3 10.5 7.1 PCB 118 <1 <1 <1 50.7 14.5 14.3 45.7 28.5 227.0 15.1 PCB 123 <1 <1 <1 4.9 1.8 2 4.46 6.6 23.8 28.0 PCB 156 <1 <1 <1 5.7 2.8 <1 3.52 4.9 24.2 22.4 PCB 157 <1 <1 <1 <1 <1 <1 <1 <1 5.0 <1 PCB 167 <1 <1 <1 3.1 1.3 <1 <1 2.6 13.7 7.9 PCB 189 <1 <1 <1 <1 <1 <1 <1 <1 1.3 <1

TABLE 1f Heavy Metals Chemical Contamination ASPIF HCPC PC PH Parameter #1 #2 #3 #1 #2 #3 #1 #2 #3 #1 Elements xLOQ xLOQ xLOQ xLOQ Aluminium 7.6 <1 88.0 99.0 76.0 dnt dnt dnt 349 503.0 Antimony <1 <1 <1 <1 <1 dnt dnt dnt 2.0 9.0 Arsenic <1 9.0 <1 <1 <1 dnt dnt dnt <1 1.0 Barium <1 <1 2.8 <1 <1 dnt dnt dnt 4.8 288.0 Bismuth <1 295 <1 <1 <1 dnt dnt dnt <1 1.0 Lead <1 <1 <1 <1 <1 dnt dnt dnt 3.0 140.0 Boron <1 3 <1 <1 <1 dnt dnt dnt 4.4 1.4 Calcium 6.2 12.0 794.0 6.2 2.6 dnt dnt dnt 56.0 690.0 Cerium <1 <1 <1 <1 <1 dnt dnt Dnt 2.0 3.0 Chromium <1 <1 7.0 <1 <1 dnt dnt dnt 7.0 45.0 Cobalt <1 <1 <1 <1 <1 dnt dnt dnt 5.0 1.0 Iron <1 <1 45.0 9.3 3.4 dnt dnt dnt 77.0 160.0 Gallium <1 <1 <1 <1 <1 dnt dnt dnt <1 1.0 Germanium <1 3.0 <1 <1 <1 dnt dnt dnt <1 <1 Iridium <1 126.0 <1 <1 <1 dnt dnt dnt <1 <1 Potassium <1 2.0 <1 <1 1 dnt dnt dnt 2.1 7.2 Copper <1 1.0 4.0 4.0 <1 dnt dnt dnt 9.0 360.0 Lithium <1 568.0 <1 <1 <1 dnt dnt dnt 3.0 3.0 Magnesium 32.0 <1 226.0 64.0 26.0 dnt dnt dnt 154.0 1172.0 Manganese <1 11.1 8.0 <1 1 dnt dnt dnt 10.0 35.0 Molybdenum <1 <1 <1 <1 <1 dnt dnt dnt <1 22.0 Sodium <1 <1 222.0 74.0 72.0 dnt dnt dnt 132.0 358.0 Nickel <1 <1 <1 <1 <1 dnt dnt dnt 4.0 6.0 Phosphorus 3.9 <1 5.9 4.0 3.9 dnt dnt dnt 2.2 6.2 Rubidium <1 3.4 <1 <1 <1 dnt dnt dnt <1 <1 Ruthenium <1 2.0 <1 <1 <1 dnt dnt dnt <1 <1 Strontium <1 8.2 8.4 <1 <1 dnt dnt dnt 2.2 17.2 Titanium 4.0 <1 36.0 4.4 3 dnt dnt dnt 80.0 7900.0 Uranium <1 240 <1 <1 <1 dnt dnt dnt <1 <1 Tungsten <1 41 <1 <1 <1 dnt dnt dnt <1 6.0 Yttrium <1 <1 <1 <1 <1 dnt dnt dnt <1 3.0 Zinc 2.0 240.0 2470.0 100.0 2920.0 dnt dnt dnt 3150 890.0 Tin <1 <1 <1 <1 <1 dnt dnt dnt <1 8.0 Zirconium <1 41.0 1.0 <1 2.0 dnt dnt dnt 4.0 48.0

TABLE 1g Organotins Chemical Contamination ASPIF HCPC PC PH Parameter #1 #2 #3 #1 #2 #3 #1 #2 #3 #1 Organotin compounds xLOQ xLOQ xLOQ xLOQ Monomethyltin 2.0 <1 <1 <1 <1 dnt dnt <1 dnt <1 Dimethyltin <1 <1 <1 4.0 <1 dnt dnt <1 dnt 5.0 Monobutyltin <1 <1 <1 4.0 5.0 dnt dnt 2.3 dnt 3.0 Dibutyltin 1.7 <1 <1 1.3 <1 dnt dnt 20.7 dnt 11.7 Tributyltin <1 <1 <1 <1 <1 dnt dnt <1 dnt 3.0 Dioctyltin <1 <1 <1 45.0 <1 dnt dnt <1 dnt 2.0

TABLE 1h Phthalates Chemical Contamination ASPIF HCPC PC PH Parameter #1 #2 #3 #1 #2 #3 #1 #2 #3 #1 Phthalates xLOQ xLOQ xLOQ xLOQ Di-2-propylheptyl phthalate <1 <1 <1 <1 <1 1.2 <1 1.7 1.2 14.6 Diethyl phthalate <1 <1 <1 <1 <1 <1 <1 <1 <1 4.6 Diisobutyl phthalate <1 <1 <1 24 9.6 1.3 12.6 6.2 6.6 22.0 Dibutyl phthalate <1 <1 <1 26 10.8 8.4 4.6 9.2 22.0 32.0 Dimethoxyethyl phthalate <1 <1 <1 <1 <1 <1 <1 <1 1.7 <1 Benzylbutyl phthalate <1 <1 <1 <1 <1 <1 <1 <1 2.6 10.4 Di-2-ethylhexyl phthalate <1 <1 <1 12.8 8.4 3.0 12.6 15.4 17.8 700.0 Diisononyl phthalate <1 <1 <1 <1 <1 <1 24 20.0 26.0 240.0

TABLE 1i PAHs Chemical Contamination ASPIF HCPC PC PH Parameter #1 #2 #3 #1 #2 #3 #1 #2 #3 #1 PAHs xLOQ xLOQ xLOQ xLOQ Acenaphthene <1 <1 <1 10 5.6 3.8 4.1 9.7 1.8 22.0 Acenaphthylene <1 <1 <1 <1.0 <1 <1 <1 8.2 <1 <1 Anthracene <1 <1 <1 1.9 1.4 2.7 <1 11.0 7.1 6.8 Benzo[a]anthracene <1 <1 <1 <1.0 <1 <1 <1 2.4 2.1 6.6 Benzo[a]pyrene <1 <1 <1 <1.0 <1 <1 <1 <1 <1 5.1 Benzo[b]fluoranthene <1 <1 <1 <1.0 <1 <1 <1 1.3 1.5 6.3 Benzo[c]fluorene <1 <1 <1 <1.0 <1 <1 <1 <1 <1 1.8 Benzo[e]pyrene <1 <1 <1 <1.0 <1 <1 <1 1.4 1.7 6.5 Benzo[g,h,i]perylene <1 <1 <1 <1.0 <1 <1 <1 1.4 1.7 12.0 Benzo[j]fluoranthene <1 <1 <1 <1.0 <1 <1 <1 <1 1.2 2.9 Benzo[k]fluoranthene <1 <1 <1 <1.0 <1 <1 <1 <1 <1 2.4 Chrysene <1 <1 <1 <1.0 <1 <1 <1 2.9 3.8 8.5 Fluoranthene <1 <1 <1 33.0 11.0 7.9 8.3 46.0 63.0 44.0 Fluorene 1.5 <1 <1 18.0 8.5 7.6 7 21.0 2.7 20.0 Indeno[1,2,3-c,d]pyrene <1 <1 <1 <1.0 <1 <1 <1 <1 <1 4.1 Naphthalene 2.4 <1 <1 6.0 <1 5.3 2.8 14.0 <1 5.7 Phenanthrene 5.2 <1 <1 59.0 27.0 28.0 18.0 120.0 62.0 100.0 Pyrene <1 <1 <1 29.0 13.0 9.2 9.9 33.0 59.0 57.0

The tested ASPIF sources were primarily absent detectable levels of chemical contaminants except for alkylphenols and heavy metals and small amounts of organotins and PAHs. The chemical contaminant results for these ASPIF sources serves as a guide for the level of chemical contamination representative of these controlled end markets and demonstrates that heavy metals, which are of low transfer risk anyway, are ubiquitous across all film sources. Hence, heavy metals were not included in ongoing analysis within this application. The tested High-Custody Post-Commercial film sources were largely free of pesticides and alkylphenol ethoxylates, but contained detectable levels of alkylphenols, bisphenol-A, dioxins/furans/PCBs, and PAHs and low levels of phthalates. The tested Post-Commercial Film sources were heavily contaminated with every class evaluated; for example, dioxins were typically as high as 40× the LOQ, but for one source, dioxins were as high as 200× the LOQ. The tested Post-Household source was the most heavily contaminated; for example, dioxins were as high as 300× the LOQ and PCBs were as high as 180× the LOQ.

From TABLES 1a-1i, representative chemical species were selected from the various classes based upon prevalence across the spectrum of reclaim sources. The selected representative chemical species within these classes include: piperonyl butoxide (representing pesticides); 4-t-octylphenolhexaethoxylate and iso-nonylphenoltriethoxylate (representing alkylphenolethoxylates); iso-nonylphenol and 4-tert-pentylphenol (representing alkylphenols); bisphenol-A (representing phenols); 1.2.3.6.7.8-HxCDD, 1.2.3.4.6.7.8-HpCDD, and OCDD (representing dioxins); OCDF (representing furans); PCB 105 and PCB 118 (representing PCBs); monobutyltin and dibutyltin (representing organotins); dibutyl phthalate and di-2-ethylhexyl phthalate (representing phthalates); and fluoranthene and phenanthrene (representing polycyclicaromatic hydrocarbons (PAHs).

In embodiments of the present invention, said chemical contaminants in said first plastic include at least one chemical contaminant and such is selected from the group comprising pesticides, alkyl phenols, alkylphenol ethoxylates, bisphenols, dioxins, furans, PCBs, phthalates, PAHs or mixtures thereof.

In embodiments of the present invention, the pesticides comprise piperonyl butoxide, BAC, DEET, and DDAC. In another embodiment of the present invention, the alkylphenol ethoxylates comprise iso-Nonylphenolmonoethoxylate, iso-Nonylphenoldiethoxylate, iso-Nonylphenoltriethoxylate, and iso-Nonylphenoltetraethoxylate. In yet another embodiment of the present invention, the alkyl phenols comprise iso-Nonylphenol, 4-tert-butylphenol, and 4-tert-Pentylphenol. In even yet another embodiment of the present invention, the bisphenols comprise bisphenol-A. In even yet another embodiment of the present invention, the dioxins comprise 1,2,3,6,7,8-HxCDD, 1.2.3.4.6.7.8-HpCDD, and OCDD. In even yet another embodiment of the present invention, the furans comprise OCDF. In even yet another embodiment of the present invention, the PCBs comprise PCB 77, PCB 81, PCB 126, PCB 105, PCB 114, PCB 118, PCB 123, PCB 156, and PCB 167. In event yet another embodiment of the present invention, the phthalates comprise di-2-propylheptyl phthalate, disobutyl phthalate, dibutyl phthalate, di-1-ethylhexyl phthalate, and diisononyl phthalate. In even yet another embodiment of the present invention, the PAHs comprise acenaphthene, acenaphthylene, anthracene, benzo[a]anthracene, benzo[b]fluoroanthene, benzo[e]pyrene, benzo[g.h.i]perylene, chrysene, cyclopenta[c.d]pyrene, flyoroanthene, fluorene, naphthalene, phenanthrene, and pyrene. In even yet another embodiment of the present invention, the organotins comprise monobutylin, dibutyltin, and dioctylin.

In embodiments of the present invention, the contaminants in the first plastic may comprise 4-tert-pentylphenol. In embodiments of the present invention, the contaminants in the first plastic may comprise bisphenol-A. In embodiments of the present invention, the contaminants in the first plastic may comprise OCDD. In embodiments of the present invention, the contaminants in the first plastic may comprise PCB 118. In embodiments of the present invention, the contaminants in the first plastic may comprise di-2-ethylhexyl phthalate.

In order to simplify the presentation of the purification results for objects of the present invention and associated examples, the number of chemical species presented per chemical class is limited to the aforementioned representative chemical species for each chemical class as shown in Table 2 along with the associated LOQ and the respective levels for the tested ASPIF sources. Note: Even though more in-depth and complete chemical analysis was completed for all objects of the present invention, only the representative chemicals are shown ongoing. This simplification does not impact or alter the inventive matter or conclusions reached from such. The specific chemicals selected, adequately and consistently represent the broader class with respect to purification.

TABLE 2 Simplified Chemical Contaminants and Associated LOQ Concentrations Parameter LOQ Pesticides Piperonyl butoxide 10 ppb Alkylphenol ethoxylates 4-t-Octylphenolhexaethoxylate 5 ppb iso-Nonylphenoltriethoxylate 50 ppb Alkylphenols iso-Nonylphenol 50 ppb 4-tert-Pentylphenol 5 ppb Bisphenols Bisphenol A 5 ppb Dioxins and dioxinlike and PCB 1,2,3,4,6,7,8-HpCDD 0.2 pptr OCDD 0.2 pptr OCDF 0.2 pptr PCB 105 5 pptr PCB 118 10 pptr Organotin compounds Monobutyltin 300 pptr Dibutyltin 300 pptr Phthalates Dibutyl phthalate 50 ppb Di-2-ethylhexyl phthalate 50 ppb Polycyclic aromatic hydrocarbons (PAH) Fluoranthene 1 ppb Phenanthrene 1 ppb

In embodiments of the present invention, the concentration of each pesticide in the purer plastic is lower than its respective LOQ; wherein the first plastic has at least one detectable pesticide. In embodiments of the present invention, the concentration of bis-phenol A in the purer plastic is lower than its respective LOQ; wherein the first plastic has at least detectable bis-phenol A. In embodiments of the present invention, the concentration of each dioxin in the purer plastic is lower than its respective LOQ; wherein the first plastic has at least one detectable dioxin. In embodiments of the present invention, the concentration of each PCB in the purer plastic is lower than its respective LOQ; wherein the first plastic has at least one detectable PCB. In embodiments of the present invention, the concentration of each phthalate in the purer plastic is lower than its respective LOQ; wherein the first plastic has at least one detectable phthalate.

In embodiments of the present invention, the concentration of piperonyl butoxide in said purer plastic is less than about 10 ppb; wherein said first plastic has a concentration of piperonyl butoxide above 10 ppb; the concentration of 4-tert-Pentylphenol in said purer plastic is less than about 5 ppb; wherein said first plastic has a concentration of 4-tert-pentylphenol is above 5 ppb; the concentration of bisphenol-A in said purer plastic is less than about 5 ppb; wherein said first plastic has a concentration of bisphenol-A is above 5 ppb; the concentration of OCDD in said purer plastic is less than about 0.2 pptt; wherein said first plastic has a concentration of OCDD above 0.2 pptr; the concentration of PCB 118 in said purer plastic is less than about 10 pptr; wherein said first plastic has a concentration of PCB 118 above 10 pptr; and the concentration of di-2-ethylhexyl phthalate in said purer plastic is less than about 50 ppb; wherein said first plastic has a concentration of di-2-ethylhexyl phthalate above 50 ppb.

In general, the efficacy of a cleaning process to remove a specific chemical contaminant is determined by the removal efficiency, defined as the difference in concentration of the chemical contaminant in the first plastic and the concentration of the chemical contaminant in the purer plastic divided by the concentration of the chemical contaminant in first plastic expressed as a percentage. However, the removal efficiency is somewhat insufficient due to the inability to determine concentrations below the LOQ. For example, if a cleaning process reduces the contamination from 2× LOQ to less than the LOQ, then the removal efficiency could be anywhere between 50% and 100%, which is a significant difference. Thus, the removal efficiency is only sufficient when the first plastic and purer plastic chemical contaminant concentration are both above LOQ. For simplicity, if the purer plastic has a chemical contaminant concentration below LOQ, then removal efficiency is calculated by assuming the chemical contaminant concentration of the purer plastic is at the LOQ and the removal efficiency is considered a minimum value and designated with >. For the above example, the removal efficiency would be calculated as 100(2× LOQ−1×LOQ)/(2×LOQ)=100(2−1)/2=50%. Thus, the removal efficiency would be >50%. In certain cases, the purer plastic will have a higher level of a contaminant than the first plastic due to 1) measurement error, 2) contaminant hot spots and cold spots in the first plastic, 3) external contamination during sampling, and 4) the purification process adds contamination. In such cases, the removal efficiency is set to 0% to not bias the average results. If such occurs consistently for a given cleaning process, then such is more likely attributable to the purification process and should be more closely examined, but such was not generally the case for the cleaning processes of the present invention.

In one embodiment of the present invention, the removal efficiency of the piperonyl butoxide contaminant is >55% wherein said piperonyl butoxide concentration in the first plastic is at least 10 parts per billion. In another embodiment of the present invention, the removal efficiency of the piperonyl butoxide contaminant is >85% wherein said piperonyl butoxide concentration in the first plastic is at least about 10 parts per billion.

In embodiments of the present invention, the removal efficiency of the 4-tert-pentylphenol contaminant is >55% wherein said 4-tert-pentylphenol concentration in the first plastic is at least 5 parts per billion. In another embodiment of the present invention, the removal efficiency of the 4-tert-pentylphenol contaminant is >85% wherein said 4-tert-pentylphenol concentration in the first plastic is at least 5 parts per billion.

In embodiments of the present invention, the removal efficiency of the bisphenol A contaminant is >55% wherein said bisphenol A concentration in the first plastic is at least 5 parts per billion. In another embodiment of the present invention, the removal efficiency of the bisphenol A contaminant is >79% wherein said bisphenol A concentration in the first plastic is at least 5 parts per billion.

In embodiments of the present invention, the removal efficiency of the OCDD contaminant is >55% wherein said OCDD concentration in the first plastic is at least about 0.2 parts per trillion. In another embodiment of the present invention, the removal efficiency of the OCDD contaminant is >95% wherein said OCDD concentration in the first plastic is at least about 0.2 parts per trillion.

In embodiments of the present invention, the removal efficiency of the OCDF contaminant is >55% wherein said OCDF concentration in the first plastic is at least about 0.2 parts per trillion. In another embodiment of the present invention, the removal efficiency of the OCDF contaminant is >93% wherein said OCDF concentration in the first plastic is at least about 0.2 parts per trillion.

In embodiments of the present invention, the removal efficiency of the PCB 118 contaminant is >55% wherein said PCB 118 concentration in the first plastic is at least 10 parts per trillion. In another embodiment of the present invention, the removal efficiency of the PCB 118 contaminant is >66% wherein said PCB 118 concentration in the first plastic is at least about 10 parts per trillion.

In embodiments of the present invention, the removal efficiency of the Di-2-ethylhexyl phthalate contaminant is >55% wherein said Di-2-ethylhexyl phthalate concentration in the first plastic is at least about 50 parts per billion. In another embodiment of the present invention, the removal efficiency of the Di-2-ethylhexyl phthalate contaminant is >78% wherein said Di-2-ethylhexyl phthalate concentration in the first plastic is at least about 50 parts per billion.

In embodiments of the present invention, the removal efficiency of the Phenanthrene contaminant is >55% wherein said Phenanthrene concentration in the first plastic is at least 1 part per billion. In another embodiment of the present invention, the removal efficiency of the Phenanthrene contaminant is >93% wherein said Phenanthrene concentration in the first plastic is at least 1 part per billion.

Contamination can be located on the surface of the plastic or in the bulk. Contamination on the surface is most readily and easily removed by surface cleaning technologies available on the market today. If the surface contamination is permeable in the plastic, then it will become bulk contamination over time through diffusion mechanisms, thus complicating reduction and limit the effectiveness of surface cleaning technologies. If the surface contamination is impermeable in the plastic, then such contamination will not diffuse into the bulk and will be reduced by simple surface cleaning methods, such as aqueous washing. Bulk contamination of either permeable or impermeable type typically cannot be effectively removed via simple surface purification methods, such as aqueous washing. Bulk contamination of the impermeable type (also known as bulk impermeable contamination) is trapped in the bulk plastic and may be freed through mechanisms comprising melt convection, melt filtration, or dissolution/disintegration of the bulk plastic.

As discussed previously, contamination can be introduced externally throughout the lifecycle of the plastic. If the contamination is impermeable, then such contamination will largely remain on the surface during the plastic lifecycle up to the point of reclaiming. If the contamination is permeable, then over time, the contamination will migrate into the bulk plastic. Thus, absent a contamination or purification event, the contamination will remain essentially constant, but the balance of surface to bulk contamination will change with time but will approach equilibrium at long time. In general, loosely bound surface contamination such as dirt may be in the 0.01 to about 0.1 wt %; whereas the chemical contamination, especially the chemical contaminants of concern for this invention, will be ppm, ppb, or even pptrillion.

Permeable and impermeable contamination represents different challenges in the demanding applications. For instance, permeable contamination whether in the bulk plastic or on the surface of the plastic will have the potential to migrate to uncontaminated materials, such as a product or to human skin. Thus, if a package contains permeable contaminants, then such contaminants will have the potential to migrate into the product and render it unsuitable for these demanding end markets. However, if the contaminant is impermeable and in the bulk of the plastic, then it will have low ability to transfer to the product or to the user's skin unless the bulk plastic is disintegrated or ingested. Thus, a package could potentially use this contaminated plastic material and not risk contamination transfer to the product or transfer directly to skin. However, if the contaminant is impermeable and on the surface of the plastic, then such contamination would have the ability to transfer to the product or skin by direct contact transfer and would be unacceptable for use in these demanding applications. Surface contamination, both permeable and impermeable, can be transformed into bulk contamination through convective mechanism, such as melt mixing and melt densification. These methods exchange or eliminate surface area with bulk material. For example, if surface contaminated film is melt-densified or melt extruded into a different shape, such as a pellet, then all original surface contamination will become bulk contamination whether such is impermeable or not and such bulk contamination will be more difficult to remove with purification processes. Melt densification is common in the recycle industry. It is also common in the recycle industry to shred incoming plastics. The latter methods generally do not convert surface contamination to bulk contamination. Ideally, surface purification methods, such as surface washing, take place on the original contaminated surface such as shredded film wherein all original surface area is reachable by the surface washing fluid.

In general, surface contamination and bulk contamination are difficult to differentiate using analytical methods. Most analytical methods for permeable chemical contaminants involve solvent extraction of the contaminant from the plastic over extended periods of time >6 hours and with exposure to extreme solvent to plastic mass ratios >100:1 and then quantifying the contaminant in the solvent using methods, such as Gas Chromatography—Mass Spectrometry (GC-MS). Such analytical methods quantify contamination but do not differentiate surface from bulk contaminants. The efficiency of a purification method to remove surface contamination can be estimated from the difference in contamination before and after the surface cleaning step but such assumes bulk contamination is not significant impacted, which is likely the case for surface washing with aqueous surface washing fluids discussed in the current invention. A more accurate way to quantify surface contamination is through washing and then solvent extraction of the contaminant at various times and then extrapolating the amount of the contaminant removed at infinitesimal time, which will approximate the amount of surface contamination. However, this method is time consuming and costly especially for contaminants that are difficult to measure in general. In addition, since the balance of surface and bulk contaminants are dynamic, it is difficult to quantify without referencing an exact sampling time. A simple method for quantifying general surface contamination (not chemical surface contamination or species based chemical contaminants) is weighing the first plastic before and after the surface washing step.

In general, bulk contamination will not be appreciably removed by simple aqueous surface washing. Permeable bulk contamination can be removed by diffusion mechanisms through gradients in chemical potential. Whereas bulk impermeable contamination is essentially trapped by the bulk polymer and methods to free the trapped contaminant comprise melt convection, melt filtration, and dissolution/disintegration of the plastic.

IV. SURFACE PURIFICATION METHODS

Surface purification methods reduce surface contamination. One such method is surface washing with a surface washing fluid that is typically water based. Surface washing is ideally completed before any melt mixing or melt densification to allow effective cleaning of the original contaminated surface. The first plastic will generally be in the form of pellets, loose or compacted film, loose or compacted flexible packages, loose or compacted rigids, loose or compacted non-wovens, etc. which will be difficult to surface wash due to excessive overall size. Hence, prior to surface washing, a granulation or shredding step is preferred. For films, it is especially important to exfoliate all available film layers, such that the washing fluid can access all original surface contamination. Thus, the size reduction step prior to surface washing should not significantly decrease the surface area to volume ratio of the reclaimed source or exchange such with new surface area. In embodiments of the present invention, said surface washing of said first plastic is conducted after a shredding or granulation step. In embodiments of the present invention, said surface area to volume ratio of the reclaimed source is preferably above about 1 mm-1, more preferably above about 5 mm-1, even more preferably above about 20 mm-1, and most preferably above about 50 mm-1. The surface washing will include significant mechanical agitation to loosen surface dirt and other contaminants to allow physical removal and transfer to the washing fluid wherein the dirt or other contaminants may or may not solubilize. As used herein, a surface washing method is any method wherein the reclaimed plastic in its original contaminated form (except for the possibility of bulk size reduction that does not eliminate more than 25% of the original surface) is contacted with an aqueous solution under mechanical agitation and then separated from the aqueous media which now contains such contamination. Such a method will in general remove the majority of loosely bound surface contamination including but not limited to dirt, wood, loosely bound paper, and some surface chemical contamination. Typical levels of loosely bound surface contamination for film based reclaimed sources are between about 0.01 and 0.1 wt %. For objects of the present invention involving a surface washed first plastic, the surface washing process will remove greater than about 80% of the loosely bound surface contamination as determined by method 2 shown in section IX.

Surface washing technologies are available extensively on the market. One representative technology is from Lindner (Lindner Washtech GmbH, Haldenfeld 4, Germany). The technology is described in detail elsewhere (https://www.lindner-washtech.com/system-solutions) but involves water washing under vigorous mechanical agitation and the potential for application of caustic to remove adhesives followed by drying and pelletization.

Another representative surface washing technology is from Herbold (Herbold Meckesheim USA, North Smithfield, R.I.). The technology is described in detail elsewhere (https://www.herbold.com/en/machines/washing-separating-drying-2/) but also involves various water washing steps under vigorous mechanical agitation followed by drying and pelletization.

Another representative technology is from Sorema (Sorema S.r.1., Anzano del Parco, Italy). The technology is described in detail elsewhere (http://sorema.it/en_US/applications/washing-line/) but involves similar aqueous operations relative to Lindner and Herbold.

Another representative surface washing technology is from Cadel called De-inking (Cadel Deinking, Alicante, Spain). The technology is described elsewhere (http://cadeldeinking.com/en/) but essentially involves the surface washing of materials using high temperature aqueous based solutions with specific surfactants, followed by water rinsing and drying. The process optional may include densification, melt filtration, de-volatilization, and pelletization following the surface washing. This method differs from other known methods in that it claims to remove surface printed inks. Such would be advantageous due to lowering the burden for chemical contaminant removal by the bulk purification methods of the current invention.

Three surface washing technologies of the prior art were evaluated for removal of the targeted classes of chemical contaminants (Comparative Examples 1, 2, and 3). Each of the surface washing technologies was evaluated using a different reclaimed film input with different levels of contamination. Overall, the surface washing technologies of the prior art were not able to purify the reclaimed materials sufficiently for use in controlled end markets. For the targeted contaminants, the commercial technologies were not able to reduce to levels near the LOQ despite low initial contamination of the respective reclaimed sources. In addition, the average removal efficiency for 4-tert-pentylphenol, bisphenol A, OCDD, PCB 118, di-2-ethylhexyl phthalate was less than about 55%.

V. MELT DENSIFICATION

The plastic coming out of the surface purification step will generally be in a similar geometric form and with similar surface area to volume ratio as the incoming reclaimed plastic, assuming the surface purification temperature was less than the primary melting point of the first plastic. For example, if the reclaimed plastic is loose film, then after shredding and surface washing at a temperature below the primary melting point of the first plastic, the film will exit surface purification as a shredded film. Because such loose plastic is difficult to feed to certain bulk purification methods such as liquid-liquid extraction, it may be desirable to melt densify such plastic prior to bulk purification. A preferred method for melt densification is melt extrusion. The melt extrusion not only densifies the plastic, but it may provide the pressure necessary for the downstream bulk purifications like liquid-liquid extraction. The melt extrusion may also include optional steps, such as melt filtration, and/or devolatilization to remove large bulk contaminants and/or volatile bulk contaminants. In addition, the molten densified plastic may be further pressurized using a melt pump. The melt pump may be necessary to increase the pressure necessary for the downstream bulk purification step. Other methods of densification are known in the art including rotating disc and rotating drum densifiers, which occur at lower temperatures relative to melt based methods.

In embodiments of the present invention, said melt densification comprises melt extrusion. In another embodiment of the present invention, said melt extrusion comprises melt filtration. In yet another embodiment of the present invention, said melt extrusion comprises melt devolatilization. In even yet another embodiment of the present invention, said melt extrusion comprises melt pumping. In embodiments of the present invention, said melt densification comprises melt extrusion, melt filtration, melt devolatilization, and melt pumping.

VI. BULK PURIFICATION

In general, bulk contamination will not be appreciably reduced by simple aqueous surface washing. Melt filtration and melt devolatilization will have the potential to remove bulk contaminants of large geometric size and remove some volatile bulk contaminants but will be largely ineffective against most bulk contaminants especially to the required levels.

One technology available on the market to complete bulk purification is InterRema Refresher™ from EREMA (EREMA Group, Ansfelden, Austria) https://www.erema.com/en/refresher/). The technology is described in detail elsewhere but essentially consists of devolatilization of pelletized materials over extended periods of time at temperatures below the primary melting point of the plastic to remove volatile organics. Most of the chemical contaminants relevant to reclaimed materials and discussed in the prior sections are highly non-volatile with normal boiling points typically above 200C. Hence, this type of devolatilization technology will have limited ability to remove most chemical contamination referenced in this application.

Other technologies based upon devolatilization are common. These may be stand-alone unit operations or combined with other operations including extrusion and melt filtration. Those utilizing sub-ambient pressure over a molten stream of the reclaimed plastic are common.

One bulk purification technology involving devolatilization was analyzed for purification capability. The technology involved slightly elevated temperatures but below the primary melting point of the plastic, long residence times (>about 2 hours), and continuous reflux of purified air to provide the devolatilization (as shown below in Comparative Example 4). The commercial devolatilization technology was unable to sufficiently remove the targeted contaminants. For example, the targeted contaminants were still well above LOQ. In addition, the average removal efficiency was ˜20%.

Extraction is a preferred bulk purification method. Extraction involves the use of a purification solvent to remove bulk permeable contaminants through creation of a chemical potential gradient between the first plastic and the solvent. The rate of permeable chemical contaminant removal will depend upon the diffusivity and solubility of the contaminant in the plastic under the conditions created in the process. For high molecular weight plastics, the diffusivity of large molecules indicative of chemical contaminants is quite low, especially in the solid state of the plastic. In addition, the solubility may be limited due to the high MW of the first plastic and lack of enthalpic mixing. Thus, the time required to remove permeable contaminants through diffusion mechanisms can be quite long and not conducive to economically viable processes at commercial scale. Methods to resolve these time scale limitations include 1). increased diffusivity through elevated temperature and/or plastic relaxation through solvent swelling, 2). decrease of diffusion path length through increased surface area to volume ratio of the first plastic exposed to the solvent, 3) increased convective transport of the contaminant through the plastic/solvent interface by: increased solubility of the contaminant in the solvent, increased partitioning of the contaminant within the solvent relative to the plastic; increased convection around the plastic/solvent interface, and increased solvent sink relative to plastic sink. The solubility of the bulk purification solvent in the plastic can be increased by operating the extraction at high pressures especially at, near, or above the critical pressure.

It is important for the extraction method to be scalable to large volumes at low cost. Hence, the time required for extraction should be low to allow for such scalability. In embodiments of the present invention, the total time for extraction is less than about 6 hours, preferably less than about 4 hours, more preferably less than about 2 hours, and even more preferably less than about 1 hour. If the extraction is completed in stages, then the time per stage may be less than this range but the overall time will still fall within these times.

Extractions may take place above, near, at, or below the primary melting point of the first plastic. Extraction taking place at, near, or above the primary melting point of the first plastic are called liquid-liquid extractions. Extractions taking place below the primary melting point of the first plastic are called leaching extractions. Extraction solvents used in leaching extractions are called leaching solvents.

In leaching processes of the current invention, the first plastic is contacted with excessive solvent during every stage and every time of the process. Such leaching processes are called flooded leaching processes. In flooded leaching processes, the mass of leaching solvent to mass of first plastic exposed to the solvent at every point in time and in every stage of the process is preferably equal to or greater than about 5:1. In certain flooded leaching processes, the solvent is rapidly stirred such that the first plastic is suspended in the solvent even when the density of the first plastic is greater than the solvent. Such flooded leaching processes 1) ensure complete contact between the surface of the first plastic and the leaching solvent and 2) lower the mass transfer resistance within the solvent boundary layer around the first plastic surface due to the convective motion. Beyond stirring, similar reduced boundary layer may be achieved in flooded leaching processes by allowing the first plastic to settle through the solvent by density gradient. Examples of flooded leaching processes include stirred tanks or the of the continuous, semi-continuous, and batch types. Additional examples of flooded leaching processes include settling tanks wherein the first plastic is allowed to settle our or through the solvent that is filled inside a tank or other vessel. The applicants have found that for flooded leaching processes of the current invention, the leaching solvent to first plastic mass ratio at any point in time and at any stage should preferably be greater than about 5:1 with more preferably being greater than 10:1 per stage and most preferably be greater than about 20:1 to enable adequate dispersion and exfoliation of the first plastic within the leaching solvent. Stirred tank extraction is an important subclass flooded leaching. For all stirred tank processes, the ability to expose the surface area of the first plastic to the leaching solvent is critical. The design of the reactor should include vigorous mechanical agitation and the potential use of extensive baffling.

For flooded leaching processes of the current invention, it may be beneficial to select a leaching solvent and operating temperature and pressure such that the leaching solvent is at its boiling point during the extraction. Such designs allow the solvent to be continuously refluxed, which may enable locally high concentration gradients as the refluxed solvent contacts the first plastic. In embodiments of the present invention, the bulk extraction is flooded leaching, and the pressure of the bulk purification is about atmospheric. In embodiments of the present invention, the bulk extraction is flooded leaching, and the pressure of the flooded leaching is about atmospheric, and the leaching solvent is at or near the normal boiling point. For polyolefin first plastics, preferred leaching solvents for flooded leaching have boiling points in the 20° C. to 90° C. range. Examples of such solvents are THF, di-ethyl ether, hexanes, acetone, ethanol, methanol, propanol, iso-propanol, MEK, and Ethyl Acetate. In embodiments of the present invention, wherein said extraction is flooded leaching in a stirred tank, the leaching solvent has a normal boiling point between 20 and 90C. In embodiments of the present invention, the leaching solvent has a normal boiling point between 20° C. and 90° C. and the flooded leaching temperature is at or near the boiling point. In another embodiment of the present invention, the leaching solvent has a normal boiling point between 20 and 90C and the purification temperature is at or near the boiling point and the pressure is at or near atmospheric. The pressure may also be higher than atmospheric for such leaching solvents. In yet another embodiment of the present invention, the leaching solvent has a normal boiling point between 20 and 90C and the pressure is above atmospheric but below 1,000 atm. The leaching solvent may also have a boiling point above the flooded leaching temperature. In even yet another embodiment of the present invention, the leaching solvent has a normal boiling point above the flooded leaching temperature. In another embodiment of the present invention, wherein said bulk purification is flooded leaching; wherein said leaching solvent is ethyl acetate; said temperature of said flooded leaching is between about 20° C. and about 120° C.; and said pressure of said flooded leaching is between about atmospheric and about 1,000 atm. In another embodiment of the present invention, wherein said bulk purification is flooded leaching; wherein said leaching solvent is hexanes; said temperature of said flooded leaching is between about 20° C. and about 120° C.; and said pressure of said flooded leaching is between about atmospheric and about 1,000 atm.

Leaching solvents with a normal boiling point below the flooded leaching temperature are also preferred due to the elevated flooded leaching pressures. In embodiments of the present invention, the leaching solvent has a normal boiling point below the flooded leaching temperature. In an embodiment of the present invention, the leaching solvent is propane. In an embodiment of the present invention, wherein said bulk purification is flooded leaching; wherein said leaching solvent is propane; said temperature of said flooded leaching is between about 20° C. and about 120° C.; and said pressure of said flooded leaching is between about 9 atm and about 1,000 atm. In another embodiment of the present invention, the leaching solvent is di-methyl ether (DME). In an embodiment of the present invention, wherein said bulk purification is flooded leaching; wherein said leaching solvent is DME; said temperature of said flooded leaching is between about 20° C. and about 120° C.; and said pressure of said flooded leaching is between about 6 atm and about 1,000 atm.

Flooded leaching solvents with normal boiling point below the flooded leaching temperature and with a critical temperature below the flooded leaching temperature are also preferred. In embodiments of the present invention, the leaching solvent has a normal boiling point below the flooded leaching temperature and has a critical temperature below the flooded leaching temperature. In an embodiment of the present invention, the leaching solvent is ethane. In another embodiment the present invention, the leaching solvent is critical or supercritical ethane. In even yet another embodiment of the present invention, wherein said bulk purification is flooded leaching; wherein said leaching solvent is ethane; said temperature of said flooded leaching is between about 31° C. and about 120° C.; and said pressure of said flooded leaching is between about 40 atm and about 1,000 atm. In yet another embodiment the present invention, the leaching solvent is CO2. In even yet another embodiment of the present invention, wherein said bulk purification is flooded leaching; wherein said leaching solvent is CO₂; said temperature of said flooded leaching is between about 31° C. and about 120° C.; and said pressure of said flooded leaching is between about 68 atm and about 1,000 atm. In even yet another embodiment the present invention, the purification leaching solvent is CO2 with <5 wt % H2O.

For flooded leaching of the current invention, the density of the leaching solvent is preferably less than the density of the first plastic at the temperature and pressure of the flooded leaching. For polyethylene reclaimed materials, the density of the leaching solvent at the temperature and pressure of the flooded leaching is preferably less than about 0.90 g/cc, but higher densities may still be used.

Preferred leaching solvents include solvents that have higher affinity for the chemical contaminants than for the first plastic. Solvents with high affinity for the chemical contaminants of interest in reclaimed polyolefins relative to the affinity of these for the polyolefins include but are not limited to diethyl ether, MEK, ethyl acetate, THF, acetone, methylene chloride, and methanol. Other oxygenated and polar hydrocarbon solvents likely have similar desired affinity. Solvents lacking such characteristics can still be used, but higher solvent to polymer ratios may be required. It is preferred that the solvent should not significantly dissolve the first plastic at the temperature and pressure of the process (<˜5 wt % may be dissolved).

In embodiments of the present invention, said leaching solvent is selected from the group comprising hydrocarbons. In another embodiment of the present invention, said leaching solvent is selected from the group comprising aliphatic hydrocarbons. In even another embodiment of the present invention, said leaching solvent is selected from the group comprising aromatic hydrocarbons. In even yet another embodiment of the present invention, said leaching solvent is selected from the group comprising alkanes.

In embodiments of the present invention, said leaching solvent is selected from the group comprising methane, ethane, propane, normal butane, isobutane, normal pentane, isopentane, neopentane, hexanes (normal hexane, isohexane, neohexane, heptanes), octanes, or mixtures thereof.

The temperature may be changed during the course of the extraction process but is generally consistent within a given stage of a unit operation. The pressure may be changed to vary solubility of the solvent in the first plastic or to increase solubility of the chemical contaminant within the solvent.

A flooded leaching extraction process may take place in stages and be combined with additional leaching extraction processes of other types not discussed in this application. The same is true for liquid-liquid extraction processes. In addition, liquid-liquid process may be combined with leaching process in various stages to form a given purification process. In embodiments of the present invention, the number of stages is more than one. In another embodiment of the present invention, the number of liquid-liquid stages is more than one. In yet another embodiment of the present invention, the number of leaching stages is more than one. In still yet another embodiment of the present invention, the number of liquid-liquid stages is one or more and the number of leaching stages is one or more. A single stirred tank reactor will achieve a certain removal efficiency. The efficiency can be improved by having multiple stirred tank reactors in series wherein the first plastic from the 1^(st) stage is predominately separated from the 1^(st) stage purification solvent and this 1^(st) stage plastic is used in the 2^(nd) stage with fresh purification solvent. This is repeated for each additional stage. This method improves the removal efficiency at the expense of additional reactors and complexity but maintains the overall time, throughput, and solvent utilization. Practically speaking, the number of reactor stages can be anywhere from 1 to ˜10 for stirred tank systems. If a larger number of stages are needed, then a continuous counter-current method may be used.

While not wishing to be bound by theory, the theoretical maximum contaminant removal capacity for a flooded leaching process is based upon the thermodynamic equilibrium/partitioning of the chemical contaminants between the first plastic and leaching solvent at the temperature and pressure of the process. Thermodynamic equilibrium may not be achieved due to kinetic limitations in the flooded leaching process. This is true for the complete flooded leaching process and is also true for each flooded leaching stage. A higher leaching solvent to first plastic mass ratio will drive both thermodynamics and kinetics in favor of purification at the expense of greater solvent consumption and greater extraction process size, which equals greater cost. Thus, a balance must be found between these important design and operational variables for the targeted chemical contaminant removal efficiency. In general, the applicants have found that the total fresh or renewed leaching solvent to first plastic mass ratio is preferably above ˜about 5:1, more preferably above ˜about 10:1, more preferably above ˜about 15:1, even more preferably above ˜about 20:1, and most preferably above ˜about 30:1 but less than about 100:1. If the flooded leaching is completed in progressive or sequential stages, then the leaching solvent to first plastic ratio per stage may be lower than this stated range (but still above the per stage minimum of ˜5:1), but the total solvent used to the total first plastic represented by the sum of solvent used in all stages should be within this range. In addition, the contaminated solvent from any stage may be used “as-is” as the solvent for another stage. Contaminated solvent at any point in the process may be renewed through known methods of distillation, filtration, ion-exchange, etc or combinations.

Another important kinetic driver is surface area to volume ratio of the first plastic within and exposed to the leaching solvent. In general, the time required to extract a chemical contaminant from a first plastic, is a strong function of the diffusion pathlength within the first plastic. The diffusion pathlength is indirectly proportional to the surface area to volume ratio of the geometrical form of the first plastic and the ability to access the surface area with leaching solvent. Hence, a higher surface area to volume ratio will produce a reduced diffusion pathlength and faster diffusion kinetics. For flooded leaching processes, a high surface area to volume ratio is a critical parameter for quick and efficient contaminant removal both surface and bulk.

For flooded leaching extractions, the surface area to volume ratio of the first plastic within and exposed to the extracting solvent is essentially identical to the surface area to volume ratio of the first plastic since the processing temperature is below the primary melting point. For film based reclaim, the flooded leaching process is ideal because of the extremely high inherent surface area to volume ratio. If reclaimed material is provided in other forms with lower surface area to volume ratio such as pellets, granulated bottles, granulated parts, etc., then it will be advantageous to increase the surface area to volume ratio by various means. These means include but are not limited to mechanical grinding, cryogenic grinding, calendaring, pressing, extension, etc. The applicants have found that the utilization of first plastics with a surface area to volume ratio of greater than ˜1 mm-1, greater than ˜5 mm-1 is preferred, greater than ˜20 mm-1 is even more preferred, and greater than ˜50 mm-1 is most preferred. In embodiments of the present invention, the surface area to volume ratio of said first plastic is greater than about 1 mm-1. In another embodiment of the present invention, the surface area to volume ratio of said first plastic is greater than about 5 mm-1. In yet another embodiment of the present invention, the surface area to volume ratio of said first plastic is greater than about 20 mm-1. In even yet another embodiment of the present invention, the surface area to volume ratio of said first plastic is greater than about 50 mm-1.

A known means for increasing the effective mass transfer through a given surface area to volume ratio and given set of conditions at the first plastic solvent interface is through applying energy to the first plastic such as but not limited to vibrational in the form of ultrasonic energy and/or microwave.

Following the bulk purification involving extraction, the plastic may be devolatilized to produce a purer plastic. The contaminated solvent will contain a small amount of dissolved purer plastic, the extracted contaminants, and the pure leaching solvent. There are many ways to recover the purer polymer and bulk purification solvent independent of the extracted contaminants.

In general, a small amount of first plastic may dissolve into the leaching solvent regardless of process type or solvent. In particular, low molecular weight waxes are particularly prone to solubilization into the extracting solvent. These may become problematic in distillation-based recovery of the purified solvent due to deposition of the waxes on process equipment. Methods are known to reduce this tendency. One such method is to lower the temperature of the contaminated solvent to below the cloud point to precipitate the polymer or wax phase followed by filtration. Unlike the first plastic, the residual plastic or waxes resulting plastic from the precipitation from the contaminated solvent may contain significant chemical.

Distillation of the contaminated bulk purification solvent may be used to regenerate the solvent for re-use in the various extraction operations. However, distillation may not be economically feasible on-going considering the high solvent volume utilized in the present invention. In addition, because the chemical contaminants of interest in this invention are extremely low in concentration, the concentration of these chemical contaminants in the contaminated solvent may be correspondingly low or even lower. Thus, a preferred method to purify the contaminated solvent is through direct removal of the contaminants without volatilizing the bulk solvent phase. Such methods include ion exchange, adsorption/absorption methods, etc. Examples include passing the contaminated solvent through a bed of activated carbon or alumina. This method can be used alone or in combination with distillation to achieve the right level of purification at the right energy consumption. In addition, the contaminated solvent from any stage may be used “as-is” as the solvent for another stage. Contaminated solvent at any point in the process may be renewed through known methods of distillation, filtration, ion-exchange, etc or combinations.

The purer plastic may contain small amounts of the solvent in either physically adsorbed or bulk absorbed form. The concentration of the solvent in the purer plastic may be reduced by devolatilization techniques. In embodiments of the present invention, said purer plastic is devolatilized to a content of <1 wt % solvent in the first plastic.

Stirred tank reactors operating at the boiling point of the leaching solvent provide improvements over existing methods. For example (Examples 1, 2, 3, and 4 and Tables 7, 8, 9, and 10), flooded leaching conducted with ethyl acetate or THF provide targeted contaminant removal efficiencies greater than about 88%.

In embodiments of the present invention, the leaching solvent is ethyl acetate. In yet another embodiment of the present invention, the leaching solvent is ethyl acetate and the process pressure is about atmospheric pressure. In another embodiment of the present invention (Example 1 Table 7), said bulk purification comprises flooded leaching in a stirred tank conducted at about 77.1° C. and about atmospheric pressure with a leaching solvent comprising ethyl acetate. In another embodiment of the present invention, said bulk purification comprises flooded leaching in a stirred tank conducted at about 77.1° C. and about atmospheric pressure with a leaching solvent comprising ethyl acetate; wherein the first plastic has a surface area to volume ratio of about 80 mm-1; wherein the number of stages is 2 and wherein the ethyl acetate to first plastic mass ratio per stage is about 18:1 and the flooded leaching time per stage is about 50 minutes for a total ethyl acetate to first plastic mass ratio of about 36:1 and for a total flooded leaching time of ˜100 minutes; wherein the average removal capacity for the contaminants, 4-tert-pentylphenol, bis-phenol A, OCDD, PCB 118, and di-2-ethylhexyl phthalate is about 89%.

In another embodiment of the present invention (Example 2 Table 8), said bulk purification comprises flooded leaching in a stirred tank involving 2 stages conducted at about 77.1° C. and about atmospheric pressure with an leaching solvent comprising ethyl acetate; wherein the first plastic has a surface area to volume ratio of about 80 mm-1; wherein the ethyl acetate to first plastic mass ratio is ˜18:1 per stage for a leaching time of ˜30 minutes per stage for a total ethyl acetate to first plastic ratio of about 36:1 and a total leaching time of about 60 minutes; wherein the average removal capacity for the contaminants, 4-tert-pentylphenol, bis-phenol A, OCDD, PCB 118, and di-2-ethylhexyl phthalate is about 89%.

In embodiments of the present invention, the leaching solvent is THF. In another embodiment of the present invention, the leaching solvent is THF and the process pressure is about atmospheric. In yet another embodiment of the present invention, said bulk purification comprises flooded leaching in a stirred tank conducted at about 66° C. and about atmospheric pressure with a leaching solvent comprising THF. In even yet another embodiment of the present invention (Example 3 Table 9), said bulk purification comprises flooded leaching in a stirred tank conducted with 2 stages at about 66° C. and about atmospheric pressure with a leaching solvent comprising THF; wherein the first plastic has a surface area to volume ratio of about 80 mm-1; wherein the THF to first plastic ratio is ˜18:1 per stage and the leaching time is ˜50 minutes per stage for a total THF to first plastic mass ratio of about 36:1 and the total leaching time is about 100 minutes; wherein the average removal capacity for the contaminants, 4-tert-pentylphenol, bis-phenol A, OCDD, PCB 118, and di-2-ethylhexyl phthalate is about 90%.

In embodiments of the present invention, the leaching solvent is DME; wherein the said flooded leaching temperature is about 70C and said flooded leaching pressure is above about 18 atm. In another embodiment of the present invention, the leaching solvent is DME; wherein the first plastic has a surface area to volume ratio of about 80 mm-1; wherein the said flooded leaching temperature is about 70C and said extraction pressure is above about 18 atm. In another embodiment of the present invention, the leaching solvent is CO2; wherein the said flooded leaching temperature is about 70C and said flooded leaching pressure is about 340 atm wherein the first plastic has a surface area to volume ratio of about 80 mm-1.

Following the flooded leaching, the purer plastic may be physically wetted with the residual solvent and potentially contain a small amount of absorbed solvent. As discussed earlier, there are many ways to recover the purer polymer and bulk purification solvent independent of the extracted contaminants. The purer polymer can be dried and devolatilized by many known commercial means. One method is through cyclonic drying. Another method is through melt extrusion with a devolatilization section. In embodiments of the present invention, the purer plastic is processed to reduce the leaching solvent to below about 1 wt % in the first plastic. The contaminated solvent can be cleaned with known methods of distillation, ion exchange, filtration, etc. The resulting devolatilized first plastic may be used as it or may be further processed into other forms including pellets via various processes.

VI. SURFACE+BULK PURIFICATION

In general, the combination of surface purification methods with bulk purification methods provide synergistic benefits to the overall removal of contamination. Surface purification methods will effectively remove surface contamination both impermeable and permeable including chemical contaminants and chemical contaminant precursors. Thus, the surface purification lowers the burden on the bulk purification and allows such to be more effective. If a first plastic is heavily contaminated with surface contamination, then such contamination is preferably removed first by a surface purification method and then followed by a bulk purification method. Once the surface purification method removes the surface contamination, the bulk purification method will remove the remaining bulk permeable contamination. The only contamination not significantly removed by this two-step approach is bulk impermeable contamination such as heavy metals that were intentionally added during original plastic part production.

Preferred methods of surface washing have already been discussed in the surface purification section. An even more preferred method of surface washing is the de-inking method also described in the surface purification method (Comparative Example 3). This method not only removes surface contamination such as dirt but also removes surface printed inks. The method is also quite effective at removing paper labels, which are chemical contaminant precursors. In this method, first plastic with the original surface area exposed is fed to a multi-step aqueous washing process where the surface contamination including surface printed inks, dirt, grit, paper, adhesives, etc. are removed. The resulting material is then dried. The dried material may be further densified into pellets using extrusion including devolatilization and melt filtration. For the purposes of this invention, a de-inking method is any surface washing method wherein said method removes surface print sufficient to produce less than about a 10% difference in the delta E between the de-inked and the unprinted first plastic (delta E measured using Method 3 in Section IX).

For nomenclature purposes, the contaminated plastic that is fed to the surface purification method will be termed the first plastic. The resulting surface purified plastic will be termed the second plastic. The second plastic will be fed to the bulk purification process and will be purified to the purer plastic. The surface purification method may involve multiple surface purification processes. The bulk purification method may involve multiple bulk purification processes of various types. The removal efficiency for the combined surface and bulk purification methods will be calculated from the first plastic concentration and the associated purer plastic.

The combination of surface washing with bulk purification technologies of flooded leaching provided an average removal efficiency for bisphenol-A, 4-tert-pentylphenol, OCDD, PCB 108, and di-2-ethylhexyl phthalate of about 95% (Example 4 Tables 10).

In embodiments of the present invention, a method to produce a purer plastic from a first plastic is presented; wherein said first plastic has a concentration of contaminants; wherein said purer plastic has a concentration of contaminants; wherein said contaminants of said first plastic comprise at least one of the following chemical classes; dioxins, PCBs, phthalates, bisphenols, and alkyl phenols; wherein said method comprises 1) a surface washing method to remove surface contamination followed by 2) an extraction conducted at a temperature and a pressure, and using a leaching solvent; wherein said extraction temperature is below the primary melting point of the first plastic called flooded leaching; wherein said leaching solvent to first plastic ratio at a given stage is greater than about 5:1; wherein said flooded leaching is conducted for a period of time and a period of time per stage; wherein said flooded leaching reduces said concentration of contaminants in said first plastic to said concentration of contaminants in said purer plastic; and wherein the average of said reductions of said concentrations of contaminants from said first plastic to said purer plastic is at least about 55% or LOQ.

In embodiments of the present invention, said extraction takes place after a surface washing. In another embodiment of the present invention, said extraction takes place after a surface washing wherein the first plastic is not densified prior to surface washing. In yet another embodiment of the present invention, said flooded leaching takes place after a surface washing; wherein the first plastic is not densified prior to surface washing; wherein the second plastic may be densified prior to the flooded leaching process.

In embodiments of the present invention, said flooded leaching uses a leaching solvent operating at a temperature and pressure; wherein said flooded leaching operates in stages; wherein said first plastic has been partially purified using a surface washing process.

In another embodiment of the present invention (Example 4 Table 10), said surface washing involves commercially available de-inking by Cadel; wherein said de-inking results in a delta E change of <10% and a removal of loosely bound surface contamination of >80%; said bulk purification comprises flooded leaching in a stirred tank conducted at about 77.1° C. and about atmospheric pressure with a leaching solvent comprising ethyl acetate with an ethyl acetate to first plastic mass fed ratio of ˜36:1 and an average leaching time of ˜60 minutes. In yet another embodiment of the present invention, said surface washing involves commercially available de-inking by Cadel; wherein said de-inking results in a delta E change of <10% and a removal of loosely bound surface contamination of >80%; said bulk purification comprises flooded leaching in a stirred tank involving 2 stages conducted at about 77.1° C. and about atmospheric pressure with a leaching solvent comprising ethyl acetate with an ethyl acetate to first plastic mass fed ratio of ˜18:1 at each stage and an average leaching time per stage of ˜30 minutes; wherein said first plastic is surface purified; wherein the purification process results in a removal efficiency for OCDD of about 98%.

In embodiments of the present invention, wherein said surface washing involves any known surface washing method; said bulk purification is flooded leaching using a stirred tank; wherein said bulk purification solvent comprises a leaching solvent. In another embodiment of the present invention, said flooded leaching extraction using a stirred tank comprises multiple leaching steps or stages.

VII. Purer Plastic

The purer plastic produced from the first plastic will have a lower level of contamination relative to the first plastic. The purer plastic from the bulk purification step may be further processed to produce a pellet or other end use material. If a pellet is desired, then such step could involve melt extrusion followed by pelletization. The melt extrusion may optionally include a melt filtration step and/or a devolatilization step. The melt extrusion may include additional ingredients to the purer plastic, such as AO, slip agents, anti-block agents, TiO₂, colorants, etc.

VIII. EXAMPLES Comparative Example 1—Purification of High-Custody Post-Commercial Film Using Commercially Available Water Wash Process #1 followed by Melt Densification

A first plastic material, consisting of High-Custody Post-Commercial Film #1, was fed into a commercially available purification process. The cleaning process consisted of shredding, various water washing steps, drying, and melt densification. The shredding homogenized the material while reducing its fundamental size. The aqueous water washing should have effectively removed surface contamination. However, the ability of this process to remove bulk permeable contamination should be minimal due to the low solubility of the chemical contaminants in the water. A small amount of volatile bulk contamination should be removed during drying and melt densification, but overall, the bulk contamination should be largely unaffected. Also, the high-custody post-commercial film source used as the first plastic had limited chemical contamination as demonstrated by the low levels of pesticides, dioxins, and phthalates. The first plastic and purer plastic were analyzed for the classes of chemical contaminants typically present in recycled materials by GALAB Laboratories GmbH (Am Schleusengraben 7, 21029 Hamburg, Germany) using the methods disclosed in section IX Methods. After purification, the purer plastic contained a slightly reduced level of chemical contamination as shown in Table 3. The removal of the five selected species were as follows: For 4-tert-pentylphenol, the removal efficiency was 0%. For bisphenol A, the removal efficiency was 94%. For OCDD, the removal efficiency was 78%. For the PCB 118, the removal efficiency was 68%. For the di-2-ethylhexyl phthalate, the removal efficiency was 22%. The average removal efficiency for the five targeted species was about 52%.

TABLE 3 Purification of High-Custody Post-Commercial (HCPC) Source #1 using Commercial Water Washing Process #1 Purer Plastic HCPC #1 After First Plastic Water Washing Removal HCPC #1 Process #1 Efficiency Parameter xLOQ xLOQ % Pesticides Piperonyl butoxide <1 <1 n.a. Alkylphenol ethoxylates 4-t-Octylphenolhexaethoxylate <1 <1 n.a. iso-Nonylphenoltriethoxylate <1 <1 n.a. Alkylphenols iso-Nonylphenol 190.0 174.0  8% 4-tert-Pentylphenol 19.4 44.0  0% Bisphenols Bisphenol A 46000.0 2800.0 94% Dioxins and dioxinlike and PCB 1,2,3,6,7,8-HxCDD <1 <1 n.a. 1,2,3,4,6,7,8-HpCDD 2.8 <1 >64%  OCDD 11.1 2.4 78% OCDF <1 <1 n.a. PCB 105 24.6 11.3 54% PCB 118 50.7 16.3 68% Organotin compounds Monobutyltin <1 <1 n.a. Dibutyltin 1.7 <1 >70%  Phthalates Dibutyl phthalate 26.0 13.2 49% Di-2-ethylhexyl phthalate 12.8 10.0 22% Polycyclic aromatic hydrocarbons (PAH) Fluoranthene 33.0 20.0 39% Phenanthrene 59.0 43.0 27%

Comparative Example 2—Purification of High-Custody Post-Commercial Film #2 Using Water Wash Process #2 Followed by Melt Densification

A first plastic material, consisting of High-Custody Post-Commercial Film #2, was fed into a purification process available on the market to produce a purer plastic. The cleaning process consisted of shredding, aqueous hot water washing, drying, and melt densification. As was the case with Water Wash Process #1, this process should remove surface contamination but be limited in ability to remove bulk permeable contamination. The first plastic and purer plastic were analyzed for the classes of chemical contaminants typically present in recycled materials by GALAB Laboratories GmbH (Am Schleusengraben 7, 21029 Hamburg, Germany) using the methods disclosed in section IX Methods, as shown in Table 4. The high-custody film source, first plastic, had limited chemical contamination as demonstrated by the low levels of dioxins, PCBs, phthalates, and PAHs. The purer plastic contained a mixture of increased and slightly decreased levels of chemical contamination. The increase in certain chemical contaminants were likely due to cross-contamination from other more heavily contaminated feed streams and/or variability in the contamination level of the current feed. The removal of the five selected species were as follows: For 4-tert-pentylphenol, the removal efficiency was 0%. For bisphenol A, the removal efficiency was 96%. For OCDD, the removal efficiency was 0%. For the PCB 118, the removal efficiency was 68%. For the di-2-ethylhexyl phthalate, the removal efficiency was 0%. The average removal efficiency for the five targeted species was about 14%.

TABLE 4 Purification of High-Custody Post-Commercial (HCPC) Source #2 using Commercial Water Washing Process #2 Purer Plastic HCPC #2 After First Plastic Water Washing Removal HCPC #2 Process #2 Efficiency Parameter xLOQ xLOQ % Pesticides Piperonyl butoxide <1 <1 n.a. Alkylphenol ethoxylates 4-t-Octylphenolhexaethoxylate <1 <1 n.a. iso-Nonylphenoltriethoxylate <1 <1 n.a. Alkylphenols iso-Nonylphenol 120.0 340.0 0% 4-tert-Pentylphenol 52.0 134.0 0% Bisphenols Bisphenol A 1800.0 72.0 96%  Dioxins and dioxinlike and PCB 1,2,3,6,7,8-HxCDD <1 <1 n.a. 1,2,3,4,6,7,8-HpCDD <1 2.4 >64%  OCDD 2.6 10.5 0% OCDF <1 <1 n.a. PCB 105 9.9 8.8 11%  PCB 118 14.5 17.4 0% Organotin compounds Monobutyltin 5.0 <1 >80%  Dibutyltin <1 <1 n.a. Phthalates Dibutyl phthalate 10.8 12.4 0% Di-2-ethylhexyl phthalate 8.4 8.4 0% Polycyclic aromatic hydrocarbons (PAH) Fluoranthene 11.0 18.0 0% Phenanthrene 27.0 40.0 0%

Comparative Example 3A—Purification of Post-Commercial #1 Film Using Commercial De-Inking Process from Cadel

A first plastic material, consisting of Post-Commercial Film #1, was fed into a purification process available on the market from Cadel called De-inking (http://cadeldeinking.com/en/) to produce a purer plastic. The process consisted of shredding, aqueous de-inking, water washing/rinsing, and drying. From the patent art, the de-inking step involves elevated temperatures, elevated pH, and surfactants. The various washing steps should effectively remove surface contamination. In addition, small amounts of bulk permeable contamination will be removed due to the elevated temperatures, which will increase the diffusivity, and the potential increase in solubility of the contaminants in the water due to the surfactant/pH combination. However, the bulk extraction was expected to be low. The incoming first plastic was determined to have 0.125 wt % loosely bound surface contamination compared to about 0.02 wt % for the purer plastic in the form of shreds. Therefore, this cleaning process removed greater than 80% of the incoming loosely bound surface contamination. After cleaning but prior to analyzing the first plastic for chemical contamination, the shreds were melt densified using a single screw extruder at 190C to produce pellets. The pellets were ground to a mass average diameter of 300 to 500 microns. The first plastic and purer plastic were analyzed for the classes of chemical contaminants typically present in recycled materials by GALAB Laboratories GmbH (Am Schleusengraben 7, 21029 Hamburg, Germany) using the methods disclosed in section IX Methods, as shown in Table 5. The first plastic contained a moderate level of chemical contamination indicative of post-commercial film lacking a high custody lifecycle. For example, the incoming dioxins like OCDD were 40× the LOQ, which is higher than the previously described high-custody sources of COMPARATIVE EXAMPLES 1, 2, and 5. In addition, this particular source has a high level of paper contamination, which has the potential to form additional chemical contamination once re-melted for densification/pelletization. This particular source was especially high in alkylphenols (˜1,000× the LOQ) further indicating the level of chemical contamination within this recycle source. This first plastic was composed of shredded film with significant portions being melted together into clumps of plastic. Hence, the effectiveness of surface washing techniques with this source will be somewhat inhibited due to the lack of access to the complete contaminated surfaces. After the deinking process, the purer plastic contained a reduced level of chemical contamination. The removal of the five selected species were as follows: For 4-tert-pentylphenol, the removal efficiency was 71%. For bisphenol A, the removal efficiency was 0%. For OCDD, the removal efficiency was 60%. For the PCB 118, the removal efficiency was 0%. For the di-2-ethylhexyl phthalate, the removal efficiency was 22%. The average removal efficiency for the five targeted species was about 31%.

Comparative Example 3B—Purification of Post-Household Film #1 Using Commercial DE-Inking Process from Cadel

A first plastic material, consisting of Post-Household Film #1, was fed into the surface purification process of COMPARATIVE EXAMPLE 3A to produce a purer plastic. The incoming first plastic was determined to have 0.047 wt % loosely bound surface contamination compared to about 0.003 wt % for the purer plastic. Therefore, this cleaning process removed greater than 80% of the incoming loosely bound surface contamination. Prior to analyzing for chemical contamination, the shreds of Post-Household Film #1 were melt densified using an extruder and pelletized. The pelletized material was ground to a mass average particle size of 300 to 500 microns. The first plastic and purer plastic were analyzed for the classes of chemical contaminants typically present in recycled materials by GALAB Laboratories GmbH (Am Schleusengraben 7, 21029 Hamburg, Germany) using the methods disclosed in section IX Methods, as shown in Table 5. The first plastic contained an extremely high level of chemical contamination including significant dirt. For example, the pesticide piperonylbutoxide was ˜7× the LOQ; alkylphenol ethoxylates were ˜1,000× the LOQ; dioxins and phthalates were ˜300× the LOQ. The purer plastic contained a reduced level of chemical contamination. Note: The difference in removal efficacy between COMPARATIVE EXAMPLES 3A AND 3B despite using identical cleaning processes were likely due to 1). differences in the surface area exposed for the cleaning process, 2). the differences in the distribution of the chemical contaminants on the surface and within the bulk, and 3). inherent variability in the chemical contaminants within a sample and variability in the measurement technique. The removal of the five selected species were as follows: For 4-tert-pentylphenol, the removal efficiency was 38%. For bisphenol A, the removal efficiency was 92%. For OCDD, the removal efficiency was 21%. For the PCB 118, the removal efficiency was 0%. For the di-2-ethylhexyl phthalate, the removal efficiency was 73%. The average removal efficiency for the five targeted species was about 45%.

TABLE 5 Purification of Post-Commercial (PC) Source #1 and Post- Household (PH) Source #1 using Commercial De-inking Purer Purer Plastic 3A Plastic 3B First PC #1 First PH #1 Plastic 3A After De- Plastic 3B After De- PC #1 inking 3A Removal PH #1 inking 3B Removal Parameter xLOQ xLOQ Efficiency % xLOQ xLOQ Efficiency % Pesticides Piperonyl butoxide 1.0 <1 >0% 6.6 <1 >68%  Alkylphenol ethoxylates 4-t-Octylphenolhexaethoxylate 5.0 <1 >80%  17.4 1.4 92% iso-Nonylphenoltriethoxylate 3.2 <1 >69%  32.0 10.2 68% Alkylphenols iso-Nonylphenol 920.0 136.0 85% 300.0 130.0 57% 4-tert-Pentylphenol 1660.0 480.0 71% 1720.0 1060.0 38% Bisphenols Bisphenol A 4.8 11.4  0% 144.0 11.0 92% Dioxins and dioxinlike and PCB 1,2,3,6,7,8-HxCDD <1 <1 n.a. 7.4 3.5 52% 1,2,3,4,6,7,8-HpCDD 3.8 3.0 20% 63.0 31.0 51% OCDD 39.6 15.9 60% 308.5 243.0 21% OCDF 5.5 2.8 49% 13.8 12.9  7% PCB 105 35.2 42.2  0% 116.4 122.6  0% PCB 118 45.7 52.6  0% 15.1 176.0  0% Organotin compounds Monobutyltin dnt dnt n.a. 3.0 dnt n.a. Dibutyltin dnt dnt n.a. 11.7 dnt n.a. Phthalates Dibutyl phthalate 4.6 <1 >78%  32.0 2.8 91% Di-2-ethylhexyl phthalate 12.6 9.8 22% 700.0 188.0 73% PAHs Fluoranthene 8.3 8.6  0% 44.0 24.0 45% Phenanthrene 18.0 11.0 39% 100.0 53.0 47%

Comparative Example 4—Purification of High Custody Post-Commercial #3 Film Using Commercial De-Odorizing Process

A first plastic material, consisting of High Custody Post-Commercial Film #3, was fed into a purification process stated to be a de-odorization technology. The process consisted of exposing the pelletized feed material to moderate temperatures and continuous air flushing. As such, this cleaning technique primarily removes volatile surface and bulk contamination. However, most of the chemical contaminants of relevance to controlled end markets are highly non-volatile. The first plastic and purer plastic were analyzed for the classes of chemical contaminants typically present in recycled materials by GALAB Laboratories GmbH (Am Schleusengraben 7, 21029 Hamburg, Germany) using the methods disclosed in section IX Methods, as shown in Table 6. The high-custody film source #3 had limited chemical contamination as demonstrated by the low levels of dioxins, PCBs, phthalates, and PAHs. The purer plastic contained a slightly reduced level of chemical contamination. The removal of the five selected species were as follows: For 4-tert-pentylphenol, the removal efficiency was 88%. For bisphenol A, the removal efficiency was 96%. For OCDD, the removal efficiency was 20%. For the PCB 118, the removal efficiency was 0%. For the di-2-ethylhexyl phthalate, the removal efficiency was 0%. The average removal efficiency for the five targeted species was about 41%.

TABLE 6 Purification of High-Custody Post-Commercial (HCPC) Source #3 using Commercial De-Odorization Purer Plastic HCPC #3 After First Plastic De- Removal HCPC #3 odorization Efficiency Parameter xLOQ xLOQ % Pesticides Piperonyl butoxide <1 <1 n.a. Alkylphenol ethoxylates 4-t-Octylphenolhexaethoxylate <1 <1 n.a. iso-Nonylphenoltriethoxylate <1 <1 n.a. Alkylphenols iso-Nonylphenol 86.0 13.0 85% 4-tert-Pentylphenol 40.0 4.8 88% Bisphenols Bisphenol A 114.0 168.0  0% Dioxins and dioxinlike and PCB 1,2,3,6,7,8-HxCDD <1 <1 n.a. 1,2,3,4,6,7,8-HpCDD 3.4 3.0 12% OCDD 8.9 7.1 20% OCDF <1 <1 n.a. PCB 105 9.2 5.3 42% PCB 118 14.3 15.9  0% Organotin compounds Monobutyltin dnt dnt n.a. Dibutyltin dnt dnt n.a. Phthalates Dibutyl phthalate 8.4 3.4 60% Di-2-ethylhexyl phthalate 3.0 10.2  0% Polycyclic aromatic hydrocarbons (PAH) Fluoranthene 7.9 9.8  0% Phenanthrene 28.0 13.0 54% In general, the established methods for purifying/cleaning films and other plastic waste including water washing, de-inking, and devolatilization are currently not able to sufficiently remove chemical contaminants, especially in sources that are high-custody. Even with high-custody sources, the chemical contamination is still present and not removed completely, which might limit end use for certain customers. Net, there is an unmet need for a cleaning technology that is capable of more completely removing chemical contamination sufficient for highly contaminated sources and for any market desiring purer recycled materials.

Example 1—Bulk Purification Using Flooded Leaching in a Stirred Tank of Post-Household Film #1 with Ethyl Acetate at Boiling and Atmospheric Pressure

2,000 grams of ethyl acetate was added to a 5 L stirred round bottom flask. The flask was outfitted with a mechanical stirrer, one reflux condenser, and one heat jacket. The mechanical stirring was set to 400 rpm. The heating jacket was controlled by a variable voltage transformer. The heat was applied to rapidly bring the ethyl acetate to boiling (˜77.1C) in about 10 minutes. After reaching the boiling point of ethyl acetate, the heat input was lowered to achieve a consistent reflux rate of ˜10 ml/min at the boiling point of ˜77.1C. Post-Household Film #1 was added to the round bottom flask which contained the boiling ethyl acetate. ˜110 to 120 grams of Post-Household Film #1 in the form of shreds was added. The shreds were ˜20 to 30 microns in thickness. Thus, the surface area to volume ratio of the first plastic was ˜80 mm-1. The stirring was sufficient to completely exfoliate the film shreds within the ethyl acetate and prevent them from agglomerating. The extraction was continued for ˜45 minutes. The stirring was terminated, and the heat was removed. The ethyl acetate was decanted from the shreds. An additional 2,000 grams of preheated fresh ethyl acetate at or near the boiling point was added to the plastic shreds in the 5 L round bottom to complete a second extraction step. Stirring was started at 400 to 500 rpm while heating was applied sufficient to reflux the ethyl acetate at ˜10 mL/min. The time to reach reflux after the addition of fresh ethyl acetate to the shreds was ˜5 minutes. The 2nd extraction continued for a total of ˜45 minutes. The stirring was stopped, and the heat removed. The ethyl acetate was decanted off and then the film shreds were placed in a filter flask w/o vacuum to further remove residual ethyl acetate. The film shreds were then dried at room temperature over-night. The leaching solvent to first plastic ratio per stage was ˜18:1 for two stages giving a total solvent to first plastic ratio of ˜36:1. The leaching time per stage was approximately ˜50 minutes per stage for a total time of ˜100 minutes. The dried film shreds were placed in a Pharma 11 mini twin-screw compounder at ˜190C to produce pellets. The pellets were then mechanically ground to a mass average particle size of ˜1 mm to produce the final purer plastic. The purer plastic was analyzed for the classes of chemical contaminants typically present in recycled materials by GALAB Laboratories GmbH (Am Schleusengraben 7, 21029 Hamburg, Germany) using the methods disclosed in section IX Methods, as shown in Table 7. For the contaminant 4-tert-pentylphenol, the removal efficiency was 93%. For the contaminant bisphenol A, the removal efficiency was 85%. For the contaminants OCDD, the removal efficiency was 97%. For the PCB 118, the removal efficiency was 90%. For the di-2-ethylhexyl phthalate, the removal efficiency was 79%. The average removal capacity for the contaminants, 4-tert-pentylphenol, bis-phenol A, OCDD, PCB 118, and di-2-ethylhexyl phthalate was 89%.

TABLE 7 Purification of Post-Household (PH) Film #1 using Continuous Stirred Tank Reactor (CSTR) Flooded Leaching with Ethyl Acetate at Boiling Point Purer Plastic PH #1 After First Plastic Ethyl Acetate Removal PH #1 Extraction Efficiency Parameter xLOQ xLOQ % Pesticides Piperonyl butoxide 6.6 <1 >85%  Alkylphenol ethoxylates 4-t-Octylphenolhexaethoxylate 17.4 <1 >94%  iso-Nonylphenoltriethoxylate 32.0 <1 >97%  Alkylphenols iso-Nonylphenol 300.0 10.0 97% 4-tert-Pentylphenol 1720.0 112.0 93% Bisphenols Bisphenol A 144.0 22.0 85% Dioxins and dioxinlike and PCB 1,2,3,6,7,8-HxCDD 7.4 <1 >86%  1,2,3,4,6,7,8-HpCDD 63.0 1.8 97% OCDD 308.5 10.0 97% OCDF 13.8 <1 >93%  PCB 105 116.4 <1 >99%  PCB 118 15.1 1.5 90% Organotin compounds Monobutyltin 3.0 5.7  0% Dibutyltin 11.7 41.3  0% Phthalates Dibutyl phthalate 32.0 <1 >97%  Di-2-ethylhexyl phthalate 700.0 150.0 79% Polycyclic aromatic hydrocarbons (PAH) Fluoranthene 44.0 <1 >98%  Phenanthrene 100.0 3.0 97%

Example 2—Bulk Purification Using Flooded Leaching in a Stirred Tank of Post-Household Film #1 with Ethyl Acetate at Boiling and Atmospheric Pressure

˜110 to 120 grams of Post-Household Film #1 in the form of film shreds (surface area to volume ratio of ˜80 mm-1) was added to a 5 L round bottom flask. The flask was outfitted with a mechanical stirrer, one reflux condenser, and one heat jacket. The mechanical stirring was set to 400 rpm. The heating jacket was controlled by a variable voltage transformer. 2000 grams of ethyl acetate was heated to the boiling point in a separate round bottom flask. The 2000 grams of boiling ethyl acetate was added to the 5 L round bottom that contained the film shreds. The heat was applied to quickly to achieve boiling conditions. The 400-rpm stirring was sufficient to prevent the film from agglomerating and to achieve good exfoliation. Once boiling was achieved (˜5 min), the heat was lowered to produce a solvent reflux rate of ˜10 ml/min at ˜77.1C. Leaching was continued for a total of 20 to 25 minutes. After ˜25 minutes, heat was removed and then the ethyl acetate was decanted from the shreds. A second 2000 grams of preheated fresh boiling ethyl acetate was added to the shreds in the 5 L round bottom to complete a second leaching stage. Stirring was started at 400 to 500 rpm while heating was applied sufficient to refluxed at 10 mL/min. The time to reach reflex was ˜5 minutes. The 2nd leaching continued for a total of 25 minutes. The heat was removed, and the stirring was stopped. The ethyl acetate was decanted off and then the film shreds were added to a filter funnel on a filter flask without vacuum. After ˜10 minutes, the shreds were placed on a baking sheet for solvent evaporation overnight. The leaching solvent to first plastic ratio per stage was ˜18:1 for two stages giving a total leaching solvent to first plastic ratio of ˜36:1. The leaching time per stage was approximately ˜30 minutes for a total time of ˜60 minutes. The dried film shreds were placed in a Pharma 11 mini twin-screw compounder at ˜190C to produce pellets. The pellets were then mechanically ground to a mass average particle size of ˜1 mm to produce the final purer plastic. The purer plastic was analyzed for the classes of chemical contaminants typically present in recycled materials by GALAB Laboratories GmbH (Am Schleusengraben 7, 21029 Hamburg, Germany) using the methods disclosed in section IX Methods, as shown in Table 8. For the contaminant 4-tert-pentylphenol, the removal efficiency was 90%. For the contaminant bisphenol A, the removal efficiency was 79%. For the contaminants OCDD, the removal efficiency was 97%. For the PCB 118, the removal efficiency was 82%. For the di-2-ethylhexyl phthalate, the removal efficiency was 98%. The average removal capacity for the contaminants, 4-tert-pentylphenol, bis-phenol A, OCDD, PCB 118, and di-2-ethylhexyl phthalate was 89%.

The overall removal efficiency of EXAMPLE 1 and EXAMPLE 2 are quite similar despite the lower leaching time for EXAMPLE 2 suggesting the leaching is solvent sink limited as opposed to time limited. Thus, the leaching can likely be operated at lower total times but with more stages and or slightly higher leaching solvent to first plastic mass ratio to improve removal.

TABLE 8 Purification of Post-Household (PH) Film #1 using Flooded Leaching in a Continuous Stirred Tank Reactor (CSTR) with Ethyl Acetate at Boiling Point Purer Plastic PH #1 After First Plastic Ethyl Acetate Removal PH #1 Extraction Efficiency Parameter xLOQ xLOQ % Pesticides Piperonyl butoxide 6.6 <1 >84.8% Alkylphenol ethoxylates 4-t-Octylphenolhexaethoxylate 17.4 <1 >94.3% iso-Nonylphenoltriethoxylate 32.0 <1 >96.9% Alkylphenols iso-Nonylphenol 300.0 14.8 95.1% 4-tert-Pentylphenol 1720.0 172.0 90.0% Bisphenols Bisphenol A 144 30.0 79.2% Dioxins and dioxinlike and PCB 1,2,3,6,7,8-HxCDD 7.4 <1 >86.4% 1,2,3,4,6,7,8-HpCDD 63.0 2.4 96.2% OCDD 308.5 10.6 96.6% OCDF 13.8 <1 >92.7% PCB 105 116.4 2.9 97.5% PCB 118 15.1 2.8 81.5% Organotin compounds Monobutyltin 3.0 5.0 0.0% Dibutyltin 11.7 22.3 0.0% Phthalates Dibutyl phthalate 32.0 <1 >96.9% Di-2-ethylhexyl phthalate 700.0 11.2 98.4% Polycyclic aromatic hydrocarbons Fluoranthene 44.0 2.3 94.8% Phenanthrene 100.0 6.4 93.6%

Example 3—Bulk Purification Using Flooded Leaching in a Stirred Reactor of Post-Household Film #1 with THF at the Boiling Point and Atmospheric Pressure

2,000 grams of THF was added to a 5 L stirred round bottom flask. The flask was outfitted with a mechanical stirrer, one reflux condenser, and one heat jacket. The mechanical stirring was set to 400 rpm. The heating jacket was controlled by a variable voltage transformer. The heat was applied to rapidly bring the THF to boiling (˜66C) in about 10 minutes. After reaching the boiling point of THF, the heat input was lowered to achieve a consistent reflux rate of ˜10 ml/min at the boiling point of ˜66C. Post-Household Film #1 was added to the round bottom flask which contained the boiling THF solvent. ˜110 to 120 grams of Post-Household Film #1 in the form of shreds was added (surface area to volume ratio ˜80 mm-1). The stirring was sufficient to completely exfoliate the film shreds within the THF and prevent them from agglomerating. The leaching was continued for ˜45 minutes. The stirring was terminated, and the heat was removed. The THF was decanted from the shreds. An additional 2,000 grams of preheated fresh THF at or near the boiling point was added to the plastic shreds in the 5 L round bottom to complete a second leaching step. Stirring was started at 400 to 500 rpm while heating was applied sufficient to reflux the THF at ˜10 mL/min. The time to reach reflux after the addition of fresh THF to the shreds was ˜5 minutes. The 2nd leaching continued for a total of ˜45 minutes. The stirring was stopped, and the heat removed. The THF was decanted off and then the film shreds were placed in a filter flask w/o vacuum to further remove residual THF. The film shreds were then dried at room temperature over-night. The leaching solvent to first plastic ratio per stage was ˜18:1 for two stages giving a total leaching solvent to first plastic ratio of ˜36:1. The leaching time per stage was approximately ˜50 minutes for a total time of ˜100 minutes. The dried film shreds were placed in a Pharma 11 mini twin-screw compounder at ˜190C to produce pellets. The pellets were then mechanically ground to a mass average particle size of ˜1 mm to produce the final purer plastic. The purer plastic was analyzed for the classes of chemical contaminants typically present in recycled materials by GALAB Laboratories GmbH (Am Schleusengraben 7, 21029 Hamburg, Germany) using the methods disclosed in section IX Methods, as shown in Table 9. For the contaminant 4-tert-pentylphenol, the removal efficiency was 98%. For the contaminant bisphenol A, the removal efficiency was 91%. For the contaminants OCDD, the removal efficiency was 96%. For the PCB 118, the removal efficiency was 67%. For the di-2-ethylhexyl phthalate, the removal efficiency was >98%. The average removal capacity for the contaminants, 4-tert-pentylphenol, bis-phenol A, OCDD, PCB 118, and di-2-ethylhexyl phthalate was 90%.

TABLE 9 Purification of Post-Household (PH) Film #1 using Continuous Stirred Tank Reactor (CSTR) Flooded leaching Extraction with THF Purer Plastic PH#1 First Plastic After THF Removal PH #1 Extraction Efficiency Parameter xLOQ xLOQ % Pesticides Piperonyl butoxide 6.6 <1 >85%  Alkylphenol ethoxylates 4-t-Octylphenolhexaethoxylate 17.4 <1 >94%  iso-Nonylphenoltriethoxylate 32.0 <1 >97%  Alkylphenols iso-Nonylphenol 300.0 5.4 98% 4-tert-Pentylphenol 1720.0 38.0 98% Bisphenols Bisphenol A 144 12.6 91% Dioxins and dioxinlike and PCB 1,2,3,6,7,8-HxCDD 7.4 <1 >86%  1,2,3,4,6,7,8-HpCDD 63.0 2.7 96% OCDD 308.5 11.1 96% OCDF 13.8 <1 >93%  PCB 105 116.4 4.1 97% PCB 118 15.1 4.9 67% Organotin compounds Monobutyltin 3.0 3.0  0% Dibutyltin 11.7 6.7 43% Phthalates Dibutyl phthalate 32.0 <1 97% Di-2-ethylhexyl phthalate 700.0 11.2 98% Polycyclic aromatic hydrocarbons (PAH) Fluoranthene 44.0 <1 >98%  Phenanthrene 100.0 3.0 97%

Example 4—Combination of Surface Washing by Cadel De-Inking and Bulk Purification Involving Flooded Leaching in a Stirred Tank Using Post-Household Film #1 and Ethyl Acetate at Boiling and Atmospheric Pressure

A first plastic material, consisting of Post-Household Film #1 was purified as in COMPARATIVE EXAMPLE 3B to produce purer plastic #1 (surface area to volume ratio ˜8 mm-1). The purer plastic #1 was fed to a bulk purification step of extraction as follows: ˜110 to 120 grams of the purer plastic from COMPARATIVE EXAMPLE 3B in the form of film shreds was added to a 5 L round bottom flask. The flask was outfitted with a mechanical stirrer, one reflux condenser, and one heat jacket. The mechanical stirring was set to 400 rpm. The heating jacket was controlled by a variable voltage transformer. 2000 grams of ethyl acetate was heated to the boiling point in a separate round bottom flask. The 2000 grams of boiling ethyl acetate was added to the 5 L round bottom that contained the film shreds. The heat was applied to quickly to achieve boiling conditions. The 400-rpm stirring was sufficient to prevent the film from agglomerating and to achieve good exfoliation. Once boiling was achieved (˜5 min), the heat was lowered to produce a solvent reflux rate of ˜10 ml/min at ˜77.1C. Leaching was continued for a total of 20 to 25 minutes. After ˜25 minutes, heat was removed and then the ethyl acetate was decanted from the shreds. A second 2000 grams of preheated fresh boiling ethyl acetate was added to the shreds in the 5 L round bottom to complete a second leaching stage. Stirring was started at 400 to 500 rpm while heating was applied sufficient to refluxed at 10 mL/min. The time to reach reflex was ˜5 minutes. The 2nd extraction continued for a total of 25 minutes. The heat was removed, and the stirring was stopped. The ethyl acetate was decanted off and then the film shreds were added to a filter funnel on a filter flask without vacuum. After ˜10 minutes, the shreds were placed on a baking sheet for solvent evaporation overnight. The leaching solvent to polymer ratio per stage was approximately 18:1 for a time of ˜30 minutes per stage. Thus, the total leaching solvent to plastic ratio was ˜36:1 and the total leaching time was ˜60 minutes. The dried film shreds were placed in a Pharma 11 mini twin-screw compounder at ˜190C to produce pellets. The pellets were then mechanically ground to a mass average particle size of ˜1 mm in diameter to produce the final purer plastic #2. The purer plastic #2 was analyzed for the classes of chemical contaminants typically present in recycled materials by GALAB Laboratories GmbH (Am Schleusengraben 7, 21029 Hamburg, Germany) using the methods disclosed in section IX Methods, as shown in Table 10. Only dioxins, furans, and PCBs were tested for this example. In consideration of the reduced data set, the species of dioxins, furans, and PCBs displayed was expanded. For the contaminants OCDD, the removal efficiency was 98%. For the PCB 118, the removal efficiency was 83%.

TABLE 10 Purification involving both Surface Washing and Bulk Purification of Post-Household (PH) Film #1 using Flooded leaching in a Continuous Stirred Tank Reactor (CSTR) with Ethyl Acetate Purer Plastic #2 Purer PH #1 Plastic #1 After PH #1 EXAMPLE 2 Surface Removal First After PH #1 Washing Removal % After Plastic Surface After and % After Removal Surface PH #1 Washing Extraction Extraction Surface % After Washing + Parameter xLOQ xLOQ xLOQ xLOQ Washing Extraction Extraction Pesticides Piperonyl butoxide 6.6 8.4 <1 <1 >85%  >85%  >85%  Alkylphenol ethoxylates 4-t-Octylphenolhexaethoxylate 17.4 1.4 <1 <1 92% >94%  >94%  iso-Nonylphenoltriethoxylate 32.0 10.2 <1 <1 68% >97%  >97%  Alkylphenols iso-Nonylphenol 300.0 130.0 14.8 5.8 57% 95% 98% 4-tert-Pentylphenol 1720 1060.0 172 36 38% 90% 98% Bisphenols Bisphenol A 144 11.0 30.0 4.2 92% 79% 97% Dioxins and dioxinlike and PCB 1,2,3,6,7,8-HxCDD 7.4 3.5 <1 <1 52% >86%  >86%  1,2,3,4,6,7,8-HpCDD 63.0 31.0 2.4 1.9 51% 96% 97% OCDD 308.5 243.0 10.6 7.2 21% 97% 98% OCDF 13.8 12.9 <1 <1  7% >93%  >93%  PCB 105 116.4 122.6 2.9 2.4  0% 97% 98% PCB 118 15.1 176.0 2.8 2.5  0% 81% 83% Organotin compounds Monobutyltin 3.0 dnt 5.0 3.7 n.a.  0%  0% Dibutyltin 11.7 dnt 22.3 6.3 n.a.  0% 46% Phthalates Di-2-ethylhexyl phthalate 700.0 188.0 11.2 6 73% 98% 99% Diisononyl phthalate 240.0 52.0 17 13.6 78% 93% 94% PAHs Fluoranthene 44.0 24.0 2.3 1.8 45% 95% 96% Phenanthrene 100.0 53.0 6.4 5.4 47% 94% 95%

Example 5—Surface Purification Steps, Melt Densification, and Bulk Purification Involving Flooded Leaching in a Stirred Reactor with Ethyl Acetate

A first plastic material, comprising shredded contaminated film having a surface area to volume ratio of greater than about 50 mm-1, is fed into a surface purification step, comprising an aqueous surface washing step while applying vigorous mechanical agitation for a time of ˜30 min; wherein the said surface washing step results in greater than about 80% of the loosely bound surface contamination. The resulting material is then conveyed into a 3-stage continuous stirred tank flooded leaching bulk purification operating with ethyl acetate at about 77C and near atmospheric pressure at a 20:1 ethyl acetate to first plastic ratio for a residence time of ˜20 minutes per stage. after the 1^(st) stage, the plastic from stage 1 is conveyed to a second tank reactor under similar conditions as stage 1. This is repeated within a 3^(rd) stage for a total solvent to feed ratio of ˜60:1 and a total extraction time of ˜60 minutes. The plastic from the third stage is de-volatilized using mechanical cyclonic action and then transported to a vented single screw extruder where the material is melted, devolatilized, and melt filtered. The resulting molten material is formed into a pellet and quenched with water or air. The resulting pellet is the purer plastic. The average removal capacity for the contaminants, 4-tert-pentylphenol, bis-phenol A, OCDD, PCB 118, and di-2-ethylhexyl phthalate is greater than about 55%.

IX. Methods

-   -   1. The following methods were used to measure the various         chemical contaminants analytically. Pesticides: the EN         15662:2018-07 Modular QuEChERS-method was applied. For         alkylphenol ethoxylates, alkyl phenols, and bisphenols the         following technique was applied: the samples were cut,         homogenized, and weighted; then, an internal standard         (deuterated bisphenol A) was added, the samples were then         extracted with hexane at room temperature, MSTFA         (N-Methyl-N-(trimethylsilyl)trifluoroacetamide) was added for         derivatization, and the contaminant level was determined by         GC-MSD. For dioxins, furans, and PCBs: the ISO/IEC 17025:2005         method was applied. The samples were cut into small pieces,         13C/12C-labeled PCDD/F internal standards to an aliquot of the         sample material were added, extraction and destroying of the         matrix by hexane and H2504 for 1 h was employed, re-extraction         with hexane (3 times for 30 min) was employed, multi-step         chromatographic clean-up was applied, 13C/12C-labeled         PCDD/F-recovery standards to the measurement solutions were         added, and quantification via the internal labelled         PCDD/F-standards (isotope dilution technique and internal         standard technique) was applied. For organotins: the method         followed the EDANA-Protocol (WSP 351) for organotin compounds in         absorbent hygiene products and their constituent raw materials.         More specifically, the samples were extracted with a sodium         diethyldithiocarbamate solution in ethanol, alkylated with         sodium tetraethyl borate, and transferred by extraction with         hexane into the organic phase. Then, the tetrasubstituted         organotin compounds were separated by using capillary gas         chromatography, proven with an AED or MS as detector. GC-ICP-MS         was used as detector system for the organometallic analysis. For         phthalates: the samples were cut, homogenized, and weighted. An         internal standard and extraction by hexane at room temperature         were then employed. The extracted phthalates were then         identified and quantified by GC-MSD. For PAHs: the samples were         cut, homogenized, and weighted. Then, an internal standard of         deuterated PAHs was added, and the samples were extracted with         hexane. The extracted PAHs were purer with silica gel,         concentrated, and then characterized by GC-MSD.     -   2. The amount of loosely bound surface contamination is         determined by the following method: Approximately 20 grams of         plastic are added to a 1,000 mL round bottom flask.         Approximately 300 mL of distilled water are added to the 1,000         mL round bottom flask. The round bottom flask is capped and then         vigorously shaken for about 60 seconds. The water is decanted         from the flask. Approximately 600 mL of additional distilled         water are added to the 1,000 mL flask and then immediately         decanted to leave the original first plastic with a small amount         of water. The first plastic is removed from the round bottom and         allowed to dry at 60C overnight in a convection oven. The % mass         change of the plastic is the amount of loosely bound surface         contamination.     -   3. Color measurements were obtained with a Minolta         Spectrophotometer, Model CM580d. The ‘white’ portion of a Leneta         card was used as a common background and as the reference point         for delta E calculations. Delta E is the color difference (dE or         4E), between a sample color and a reference color. Color         measurements were taken using a D65 illuminant and a 10°         observer. A minimum of three measurements were taken for each of         the compressed thermoplastic starch composition samples. L, a, b         values are averaged and reported along with ΔE values. ΔE values         for the pure white Leneta card are zero and positive deviations         from zero indicate increased discoloration. Those skilled in the         art will know how to calculate the delta E value.

The foregoing description is given for clearness of understanding only, and no unnecessary limitations should be understood therefrom, as modifications within the scope of the invention may be apparent to those having ordinary skill in the art.

The dimensions and values disclosed herein are not to be understood as being strictly limited to the exact numerical values recited. Instead, unless otherwise specified, each such dimension is intended to mean both the recited value and a functionally equivalent range surrounding that value. For example, a dimension disclosed as “40 mm” is intended to mean “about 40 mm.”

Every document cited herein, comprising any cross referenced or related patent or application, is hereby incorporated herein by reference in its entirety unless expressly excluded or otherwise limited. The citation of any document is not an admission that it is prior art with respect to any invention disclosed or claimed herein or that it alone, or in any combination with any other reference or references, teaches, suggests or discloses any such invention. Further, to the extent that any meaning or definition of a term in this document conflicts with any meaning or definition of the same term in a document incorporated by reference, the meaning or definition assigned to that term in this document shall govern.

While particular embodiments of the present invention have been illustrated and described, it would be obvious to those skilled in the art that various other changes and modifications can be made without departing from the spirit and scope of the invention. It is therefore intended to cover in the appended claims all such changes and modifications that are within the scope of this invention. 

What is claimed is:
 1. A method to extract contaminates from a first plastic to produce a purer plastic comprising: a. providing a first plastic comprising individual contaminants, each individual contaminant having a concentration; b. extracting said individual contaminates from said first plastic at a temperature and a pressure, using ethyl acetate, in extraction stages, wherein the total extraction time is less than about 6 hours, to produce a purer plastic comprising individual contaminates, each having a concentration; wherein said extraction is flooded leaching wherein said temperature is between about 20 and 90 C; wherein said extraction stages are conducted at an ethyl acetate a to first plastic mass ratio; wherein said ethyl acetate to first plastic mass ratio per stage at any time is greater than about 5:1 but less than 100:1; wherein said pressure is between about atmospheric and 1,000 atm; wherein said first plastic individual contaminants comprise at least one of 4-tertpentylphenol, bisphenol A, OCDD, PCB 118, and 2-ethylhexyl phthalate; wherein each individual contaminants concentration in said purer plastic is reduced compared to each individual contaminants concentration in said first plastic; and wherein the average of said reductions of said concentrations of said first plastic contaminants to said purer plastic contaminants is at least about 55% or LOQ; and wherein ethyl acetate should not significantly dissolve the first plastic at the temperature and pressure of the process.
 2. The method of claim 1, wherein said number of stages is between about 1 and about
 50. 3. The method of claim 1, wherein said first plastic is a reclaimed plastic comprising at least one of a post-industrial or post-consumer film.
 4. The method of claim 1, wherein said first plastic has a mass average surface area to volume ratio of at least about 1 mm-1.
 5. The method of claim 1, wherein said first plastic is surface washed in a non-densified state by a surface washing process or processes prior to extraction and wherein said surface washing process or processes results in a greater than about an 80% reduction in loosely bound surface contamination; wherein said first plastic prior to surface washing has a surface area to volume ratio of greater than about 1 mm-1.
 6. The method of claim 5, wherein said surface washing process is of the de-inking type; wherein said de-inking process results in a delta E percent change of less than about 10% between the de-inked first plastic and the first plastic without surface printed ink.
 7. The method of claim 1, wherein said leaching solvent is purified after said flooded leaching or said flooded leaching stage or stages to allow re-use in the flooded leaching process by a solvent purification process or processes; wherein said solvent purification process or processes comprises at least one stage of physical adsorption or absorption of the chemical contaminants from the contaminated leaching solvent.
 8. The method of claim 1, wherein said first plastic is a reclaimed plastic that is at least one of a post-industrial or post-consumer film; wherein said post-consumer film includes post-commercial film and/or post-household film.
 9. The method of claim 1, wherein said pressure is about atmospheric.
 10. The method of claim 9, wherein said temperature is about the normal boiling point of ethyl acetate.
 11. The method of claim 1, wherein said pressure is above atmospheric.
 12. The method of claim 11, wherein said temperature is above the critical temperature of ethyl acetate.
 13. The method of claim 1; wherein said first plastic is surface washed in a non-densified state by a surface washing process or processes prior to extraction and wherein said surface washing process or processes results in a greater than about an 80% reduction in loosely bound surface contamination comprising at least one of 4-tertpentylphenol, bisphenol A, OCDD, PCB 118, and 2-ethylhexyl phthalate; wherein said first plastic prior to surface washing has a surface area to volume ratio of greater than about 1 mm-1.
 14. The method of claim 1; wherein said first plastic is surface washed in a non-densified state by a surface washing process or processes prior to extraction and wherein said surface washing process or processes results in a greater than about an 80% reduction in loosely bound surface contamination comprising at least one of 4-tertpentylphenol, bisphenol A, OCDD, PCB 118, and 2-ethylhexyl phthalate; wherein said first plastic prior to surface washing has a surface area to volume ratio of greater than about 1 mm-1; wherein said surface washing process is of the de-inking type; wherein said de-inking process results in a delta E percent change of less than about 10% between the de-inked first plastic and the first plastic without surface printed ink.
 15. The method of claim 1; wherein said flooded leaching is a continuous stirred tank; wherein said first plastic is surface washed in a non-densified state by a surface washing process or processes prior to extraction and wherein said surface washing process or processes results in a greater than about an 80% reduction in loosely bound surface contamination comprising at least one of 4-tertpentylphenol, bisphenol A, OCDD, PCB 118, and 2-ethylhexyl phthalate; wherein said first plastic prior to surface washing has a surface area to volume ratio of greater than about 1 mm-1; wherein said surface washing process is of the de-inking type; wherein said de-inking process results in a delta E percent change of less than about 10% between the de-inked first plastic and the first plastic without surface printed ink; wherein said continuous stirred tank involves 3 stages; wherein said temperature is about 77 C and near atmospheric pressure; wherein said ethyl acetate to first plastic ratio is about 20:1 per stage and for a residence time of about 20 minutes per stage; wherein the first plastic is de-volatilized and densified using melt extrusion to produce a purified pellet. 